The aerosol optical properties, classification and radiative forcing were examined at Panyu, the main atmospheric composition monitoring station in the Pearl River Delta (PRD)region of China.Aerosol optical properties from 2006-2012 were derived by sunphotometer measurements, which were then used as input to a radiative transfer model to calculate broadband radiation.The major results are as follows: (1) High aerosol loading prevails in the dry seasons (October to the following February) of the PRD region and the particles are majority of find-mode and strong absorption.the mean AOD500mm equals to 0.535 with more frequency of high values in October and in February than in the other months.The mean value of SSA440nm is 0.87 and more than 80% of SSA440nm ranged from 0.8 to 0.92.The mean value of AE470-870nm is 1.33, and the aerosols are dominated by fine-mode pollutions(AE470-870nm>l.2, ~84.66%) with low occurrence of floating dust particles (0.75< AE470-870nm
其他文献
"国际热核聚变实验堆(ITER)计划"是目前全球规模最大、影响最深远的国际合作项目之一.ITER装置是一个能产生大规模核聚变反应的超导托克马克,俗称"人造太阳".ITER装置中最
会议
在常压条件下,650-1000℃的温度范围内制备的MgB2块材和线带材中均存在大量孔洞,使其密度远低于MgB2的理论密度。经过十年大量系统的研究,发现高能球磨和元素掺杂是提高M
会议
氧化物高温超导单畴块材所特有的被动型磁悬浮性质正受到电工技术领域的高度关注,已经在诸如磁悬浮列车试验装置、磁悬浮轴承等技术领域得到应用.为了进一步拓展该类材料
对涂层导体而言,制备兼具良好机械性能和磁性能的立方织构NiW合金基带是目前研究中面临的巨大挑战。本文综述了我研究小组近年来以RABiTS路线制的不同高W含量Ni合金基带和
Effect of sintering time on the performance of phase formation and superconductivity of Nb3(Al,Ge) p
In early experiments, we have studied the effect of nominal chemical composition and sintering temperature phase formation and superconductivity of Nb3(Al1-
会议
通过采用XRD和背散射电子衍射技术,系统研究了无铁磁性CuNi合金和Ni9W合金基带再结晶过程中微观组织和织构的演变,对比阐明了两者再结晶织构的形成.研究结果表明:经大应变
会议
为了获得高的电流密度与钉扎能力,我们采用MOD法在LAO单晶基板上制备了多元纳米颗粒掺杂的YBCO超导薄膜。此过程中关键的难题是解决高掺杂量下,掺杂颗粒过大或薄膜引入应力
会议
第二代高温超导体由于其具有高的超导转变温度和临界电流密度使其在超导限流器等有潜在的应用.本文使用卷对卷MOCVD走带系统制备高温超导带材(Gd,Y)BCO,并通过AES、XRD、
会议
金属有机沉积法制备钇钡铜氧超导膜具有设备简单、组分易于控制及易于大面积批量制备等优势,因而成为第二代高温超导涂层导体超导层主要的制备方法之一。在提高产业化效率