Among the existing cathode materials,V2O5 is a promising cathode candidate because of its high energy density,abundance,easy synthesis,as well as low cost.However,due to quite low diffusion coefficien
【机 构】
:
New Materials R&D Center,Institute of Chemical Materials,China Academy of Engineering Physics,Mianya
论文部分内容阅读
Among the existing cathode materials,V2O5 is a promising cathode candidate because of its high energy density,abundance,easy synthesis,as well as low cost.However,due to quite low diffusion coefficient of lithium ions (10-12-10-13 cm2 s-1),irreversible phase transitions during deep discharge,and vanadium dissolution into the electrolyte,the practical use of V2O5 as a cathode material shows poor rate capability and cycling stability1,2.
其他文献
自从1997年,Goodenough等[1]研究橄榄石型结构磷酸铁锂 (LiFePO4),十多年来,其制备工艺日趋成熟,商业化进展迅速.受LiFePO4成功应用的影响,橄榄石结构磷酸盐家族的另一种重要材料—磷酸锰锂 (LiMnPO4) 越来越受到人们的关注.
Microflower structural δ-MnO2 assembled by ultrathin nanosheets grown on three dimentional graphene nanosheets is synthesized for the first time.Herein,high conductive graphene networks (Figure 1a) ma
采用草酸沉淀法制备了一系列不同镍掺杂量的锂离子电池正极材料LiNi0.5-xMn1.5+xO4(0≤x≤0.45),研究了Ni/Mn比对于材料结构及性能的影响.X射线衍射(图1)结果显示:在x为0到0.45的范围内,所有样品都呈现尖晶石结构,随着Ni/Mn比的减小,衍射峰向高角度发生了轻微的移动,晶胞参数从x=0时的8.166(A)逐步增大到x=0.45时的8.214(A)(表1),说明镍的减少可
目前,可移动电子设备及电动汽车对电池提出更高的要求,需要电池往高能量密度发展,不同类型的高电压、高容量正极材料得到了广泛的研究.在诸多正极材料中,尖晶石型的LiNi0.5Mn1.5O4以其高电位(4.7Vvs Li/Li+),良好的可逆容量(大约135mAh/g)等优异的性能[1]表现得到了广大的关注.
LiNi0.5Mn1.5O4 (LNMO) material,with a theoretical capacity of 147 mAh g-1 and a high discharge voltage (4.7 V vs.Li/Li+) plateau,has emerged as a promising cathode material for high energy density lit
通过液相沉淀法结合高温固相法制备了Sm掺杂的LiFePO4/C,测试结果表明少量Sm掺杂能够优化颗粒形貌,减小极化过电势和传荷电阻,从而提高了材料的电化学性能.大量的Sm掺杂会形成过多的SmPO4能够阻碍材料的电化学性能.电化学测试结果表明LiFe0.99Sm0.01PO4/C在1C,2C,5C和10C下的放电容量分别为148.1,133.4,117.5和106.6mAh g-1.并且材料具有很好
LiMn1-xTixO2 (x =0,0.01,0.02,0.03) cathode materials were successfully prepared by the hydrothermal treatment of Mn2O3 and TiO2 with excess LiOH·H2O aqueous solution at 150℃.The crystal structure and
As a promising cathode materials,LiFePO4 [1] received much attentions owing to its low cost,environmental compatibility,reasonable theoretical specific capacity (ca.170 mAhg-1),acceptable operating vo
The thermal stability of a FeF3 cathode was studied by differential scanning calorimetry (DSC).The lithiated electrode was found to be more thermally stable than delithiated one.On the other hand,the
Since commercialization in 1990,the rechargeable lithium-ion batteries (LIBs) are widely used as power sources for mobile telephones,computers,toys and so on.However,extending electrode materials for