【摘 要】
：
高强度TRIP钢有高的屈服强度、抗拉强度和延展性以及冲压成形能力等优点,广泛应用于汽车制造中。对不同焊接条件下HC420/780TR焊接接头进行性能检测和微观分析,结果表明:1.8mm厚HC420/780TR与1.8mm厚HC420/780TR搭接焊缝未熔合长度约2mm,接头杯突性能较差;降低接头碳当量,减弱冷裂纹倾向,让1.8mm厚HC420/780TR与1.8mm厚SPCC过渡焊,焊缝未熔合部
【机 构】
：
马鞍山钢铁股份有限公司汽车板推进处,安徽 马鞍山 243000
【出 处】
：
第十届中国钢铁年会暨第六届宝钢学术年会
论文部分内容阅读
高强度TRIP钢有高的屈服强度、抗拉强度和延展性以及冲压成形能力等优点,广泛应用于汽车制造中。对不同焊接条件下HC420/780TR焊接接头进行性能检测和微观分析,结果表明:1.8mm厚HC420/780TR与1.8mm厚HC420/780TR搭接焊缝未熔合长度约2mm,接头杯突性能较差;降低接头碳当量,减弱冷裂纹倾向,让1.8mm厚HC420/780TR与1.8mm厚SPCC过渡焊,焊缝未熔合部分减少至0.5mm,杯突性能有所改善;对1.8mm厚HC420/780TR与1.8mm厚SPCC过渡焊后进行接头热处理,降低焊接应力,焊缝未熔合长度进一步减少至0.3mm,杯突性能完全合格。
其他文献
A twinning-induced plasticity(TWIP)steel was subjected to cold rolling followed by recovery heat treatment,forming a nanotwinned steel.During the recovery annealing,the nanotwins are thermally stable
电磁监测卫星主要用于实时监测空间电磁环境状态变化,对预测地震发生有重要意义.其监测需利用伸杆机构将探测载荷伸展至远离星体的位置,弹性卷筒用作为伸杆机构的核心部件,具有展开自驱动、展开长度长(可达15m以上)、驱动力稳定、指向性高、刚度高、重量轻、储能高等优点,成为近年来的发展趋势,但其成难难度很高.本文首次提出采用拉压复合连续弯曲成形的概念用于成形此构件,并对其成形原理进行了阐述,对其成形工艺进行
动态电压恢复器是一种串联型电压补偿装置,该装置能够在很短的时间内检测到电网电压跌落,然后输出一个补偿电压使负荷电压恢复到跌落前的状态.其中储能单元为动态电压恢复器提供补偿期间所需的能量,其成本也一定程度上限制了DVR的推广.首先,本文分析了现有DVR补偿策略对储能单元电压及容量的要求,并指出这三种补偿策略的优势与不足.在此基础上,本文提出了一种新的电压补偿策略.该策略综合了常见补偿策略的优点,通过
在200℃/s的退火超快冷条件下,研究了高强冷轧薄板在退火温度为820℃时,不同时效温度对低合金高强钢组织和性能的影响。实验结果表明:随着时效温度的升高,实验用钢的抗拉强度呈现下降趋势,屈服强度呈现上升趋势,当时效温度从240℃提高到320℃时,抗拉强度从893MPa下降到了773MPa,下降了13％,屈服强度从496MPa增加到了577MPa,提升了16％。延伸率呈现上升趋势。随着时效温度的升高
In allusion to the strip deviation problem of strip cold rolling mill in the rolling production process,due to the strip asymmetric wave shape,cross wedge,equipment installation deviation and unreason
Considering the problems caused by entrance strip shape of instability during the rolling process and quality of exit strip shape,this paper proposed a strip shape feed-forward control method based on
With reference to the problem of strip running deviation caused by non symmetrical wave of incoming strip,cross wedge,equipment installation accuracy deviation,unreasonable process and etc in the cold
Oxidation kinetics of two stainless steels was studied at 1000?1150°C from 0 to 600 s in humid air containing 18%water vapour by a Thermo Gravimetric Analysis(TGA).Incubation time decreases significan
The Mo-alloyed invar alloy is prepared by the vacuum induction melting furnace.The investigations of mechanical properties,phase constitutions,microstructures,thermal expansion features are performed.
本文针对国内某特钢厂所生产的电渣重熔GCr15轴承钢轧材化学成分及夹杂物特性进行研究,并对其化学成分变化的原因、夹杂物成分与化学成分的关系进行分析。结果表明:电渣重熔后轧材Al、Si含量相对母材出现一定程度的降低,轧材氧含量相对母材出现一定程度的增加;Al烧损程度越大,钢中氧含量越高;钢中夹杂物主要以单一Al2O3,xMgO.yAl2O3,xCaO.yAl2O3为主,并含有少量以Al2O3为核心,