【摘 要】
：
A two-step manufacturing technology of composite nano-modified additive was developed.At the first stage a suspension was prepared by ultrasonic dispersion of MWCNT aggregates in isopropyl alcohol.At
【机 构】
：
Construction materials department, Kazan State University of Architecture and Engineering, Kazan 420
【出 处】
：
The 14th International Congress on the Chemistry of Cement (
论文部分内容阅读
A two-step manufacturing technology of composite nano-modified additive was developed.At the first stage a suspension was prepared by ultrasonic dispersion of MWCNT aggregates in isopropyl alcohol.At the second stage the obtained suspension was mixed with superplasticizer over the optimal time to evaporate the residual isopropyl alcohol and get a homogeneous mixture.According to the results of optimization of the cement stone composition the optimal dosage of MWCNT was established at 0.0005% mass concentration.The acceleration of hydration processes in cement stone modified with admixture is proven, because the maximal hydration temperature was higher by 12 and 14℃ for "Graphistrength" and "Taunit", respectively, than that for the control sample.The results of comparative studies are presented for the 0.0005 and 0.05% MWCNT composite additives effect on the early process of structure formation in one-day-old cement stone.It was carried out for cleaved samples at four scales: macro, meso,micro and nano, using Merlin scanning electron microscope.
其他文献
Urban structures are naturally degraded by climatic activity, saline environments and microorganisms.The last of these accelerates dissolution processes, thus generating pathologies such as the darken
In Recent years, it is necessary to reduce carbon dioxide (CO2) emissions in terms of environmental impact reduction.Concrete is material which discharges many CO2 in concrete manufacturing fields.Esp
The mechanism of external sulfate attack (ESA) involves chemical, physical and mechanical processes.Furthermore, ESA is mostly studied on saturated matured sample.However, most concrete structures are
In Polish climatic conditions frost resistance of concrete is one of its most important durability properties.There are many material and technological factors influencing on that property of concrete
Alkali silica reaction, ASR is still a durability problem in Japan although countermeasures have been established since 1986.The problems of this Japanese situation are thought to be caused by lack of
The Ordinary Portland cement (OPC)-calcium aluminate cement (AC)-arhydrite (C (S)) system is useful for various construction materials because it can provide optimal physical properties by adjusting t
In recent years, alkali-activated slag (AAS) as an alternative low-carbon cementitious material has received increased attention.However, the high shrinkage and the crack tendency of AAS limit its wid
Reinforced concrete structures should be designed in order to resist all possible loading conditions and all predictable environmental impacts and combinations thereof during the entire design service
The structural condition of solidifying binding system has various thermodynamic stability and the degree ot ordering.It predetermines the tendency of these systems to self-organizing.Self-organizing
Low water requirement cements (LWRC) are a new type of hydraulic cements obtained by co-grinding of Portland cement clinker, gypsum and water reducing agent (plasticizer).During the grinding, in the p