Electrochemical and Hard X-ray Photoelectron Spectroscopic Study on Oxide Films Formed on Alloy 600

来源 :The 4th International Symposium on Materials and Reliability | 被引量 : 0次 | 上传用户：Toowell_Star

【摘要】

：

Oxide films on Alloy 600 and Alloy 690 formed during exposure to the solution containing 500 ppm B + 2 ppm Li with or without dissolved hydrogen were characterized using photo electrochemical current

【作者】

：

Shinji Fujimoto

【机构】

：

Division of Materials and Manufacturing Science, Graduate School of Engineering,Osaka University 2-1

【出处】

：

The 4th International Symposium on Materials and Reliability

【发表日期】

：

2015年8期

下载到本地 , 更方便阅读

下载此文赞助VIP

声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架

论文部分内容阅读

　　Oxide films on Alloy 600 and Alloy 690 formed during exposure to the solution containing 500 ppm B + 2 ppm Li with or without dissolved hydrogen were characterized using photo electrochemical current response andhard X-ray photoelectron spectroscopy.

其他文献

Failure Analysis and Countermeasures Discussion of a Cracked Leak off Tube in Primary Heat Transport

Chemical composition analysis, microstructure analysis, macro and micro fracture morphology analysis were conducted on a cracked leak off tube in primary heat transport and heavy water collection syst

会议

nuclear power plantsfailure analysisconcentrationstress corrosion crackcorro

The Stress Corrosion Cracking Behavior of Simulated Reactor Components Welded 304L Stainless Steel i

Welded 304L stainless steel is the weak link in pressurized water reactor (PWR) components, Stress corrosion cracking (SCC) of simulated reactor components welded 304L stainless steel in 5mg/L chlorid

会议

stress corrosion cracking (SCC)slow strain rate testing(SSRT)welded 304L stain

核级316LN不锈钢在一回路不同水化学条件下的疲劳及应力腐蚀性能

采用直流电压降测量裂纹长度的方法,研究了316LN不锈钢管道在不同的一回路水化学条件下的疲劳和应力腐蚀开裂规律.实验结果发现,316LN的疲劳裂纹扩展速率随载荷比和频率的降低而下降,不同的水化学条件下,材料的应力腐蚀裂纹扩展速率受溶解氧影响显著.在通入2ppm氧气的条件下,材料在含B-Li水中的裂纹扩展速率最高,而在含氢水中材料裂纹扩展速率受水中溶质的影响很小.

会议

控氮不锈钢一回路管道疲劳裂纹应力腐蚀压水堆核电厂

Effect of Zinc Addition to Simulated Primary Water on SCC Susceptibility of 316L Stainless Steel

Austenitic stainless steel 316L has been well used as one of the structural materials of components in the nuclear reactor.However, severe SCC phenomenon has been found during the service.It is sugges

会议

316L stainless steelstress corrosion crackslow strain rate testzinc addition

Finite Element Simulation and Experimental Investigation of Welding Residual Stress for PWR Safe-End

A 3-D sequential coupling finite element simulation is performed to investigate thetemperature field and residual stress in the dissimilar metal weld of a PWR safe-end and nozzle.Chemical compositions

会议

safe-endwelding residual stressFEMexperimental investigation

国产52合金异种金属焊接材料高温水应力腐蚀裂纹扩展试验研究

目前国内外新建压水堆核电厂中,反应堆压力容器接管与主管道安全端之间主要采用52合金焊材焊接,经工厂焊接后成为可实际应用于核电厂的焊接件.国外实验室研究结果表明,国外52合金异种金属焊接(52Mw)材料在模拟压水堆一回路高温水环境中出现应力腐蚀裂纹扩展,裂纹扩展速率比82/182合金异种金属焊接材料低2个数量级.本文对国产52Mw合金异种金属焊接材料应力腐蚀裂纹扩展行为进行了试验研究.结果表明,国产

会议

压力容器焊接材料应力腐蚀裂纹扩展速率压水堆核电厂

Air Oxidation of Hastelloy X superalloy and FeCoNiCrAl High-entropy Alloy at 950℃

The oxidation behavior of welded HastelloyXsuperalloy, containing the substrate(X-SUB),heat-affected zone (X-HAZ) and the melt zone (X-MZ) and as-cast FeCoNiCrAl high-entropy alloy (H5-HEA)was studied

会议

OxidationHastelloy XFeCoNiCrA1 high-entropy alloyAl2O3Cr2O3MnCr2O4

Progressive Degradation of Alloy 690 and the Development of a Significant Improvement in Alloy 800CR

The present most widely used alloys for tubing in steam generators and structural materials in water cooled reactors are Alloy 690 and Alloy 800.However, both alloys, while improved over Alloy 600 may

会议

IASCC Study of Proton-irradiated Type 316 Stainless Steels in PWR Water

A management of irradiation-assisted stress corrosion cracking (IASCC) of intemal components of a nuclear power plants is considered critical for long-term operation of these reactors.Some cracking of

会议

High-Resolution Characterization of Corrosion of Nuclear Fuel Cladding Alloys

As part of the MUZIC2 project, several high resolution analysis techniques have been used to study the microstructure of a range of commercial and developmental Zr alloys under autoclave simulated PWR

会议

Electrochemical and Hard X-ray Photoelectron Spectroscopic Study on Oxide Films Formed on Alloy 600

与本文相关的学术论文