【摘 要】
：
In this study,recovery processes of isotactic polypropylene(iPP)melted spherulites at 135 ℃ after melting at higher temperatures(170–176 ℃)were investigated with polarized optical microscopy and Fouri
【机 构】
：
National Synchrotron Radiation Laboratory,College of Nuclear Science and Technology,University of Sc
【出 处】
：
The 11th International Symposium on Polymer Physics(PP2014)(
论文部分内容阅读
In this study,recovery processes of isotactic polypropylene(iPP)melted spherulites at 135 ℃ after melting at higher temperatures(170–176 ℃)were investigated with polarized optical microscopy and Fourier transform infrared spectroscopy.The recovery temperature was fixed to exclude the interference from heterogeneously nuclei.After melting at temperatures between 170 and 174 ℃,the melted spherulite could recover back to origin spherulite at the low temperature.Interestingly,a distinct infrared spectrum from those of iPP melt and crystal was observed in the early stage of recovery process after melting at low temperatures,where only IR bands resulting from short helices with 12 monomers or less can be seen,which indicates that the presence of crystal residues is not the necessary condition for the polymer memory effect.Avrami analysis further indicated that crystallization mainly took place in melted lamellae.After melting at higher temperatures,melted spherulite cannot recover.Based on above findings,we proposed that the memory effect can be mainly ascribed to melted lamellae,during which crystalline order is lost but conformational order still exists.These conformational ordered segments formed aggregates,which can play as nucleation precursors at low temperatures.
其他文献
Considering anisotropy and influence on shape memory characteristics caused by addition of carbon fiber,this work aims to describe the shape memory cycle and properties in three point bending deformat
Block copolymer is a special type of copolymer that comprises two or more chemically distinct polymer blocks covalently linked together.This special structure endows the block copolymer a variety of u
A possible two steps mechanism was proposed for crystallization during polymerization of cyclic butylenes terephthalate(CBT)(Figure 1).In such scenario(Figure 2),the catalyst was introduced into the e
The elastic properties of a self-assembled bilayer membrane are studied using the self-consistent field theory,applied to a model system composed of flexible amphiphilic chains dissolved in hydrophili
Understanding the relaxation dynamics of entangled branched polymers is highly desired for developing quantitative theories for describing the rheology of entangled polymer melts.Such understanding is
Polymer film with porous structure is a kind of material with wide applications in fields such as membrane technology,biomedical engineering,surface and coating.The porous structure of polymer film ca
A series of microgel particles composed of a polystyrene (PS) core and thermo-sensitive poly (N-isopropylacrylamide) (PNIPAM) shell with different shell thicknesses were investigated to elucidate the
We have studied the chain conformation and adsorption behavior of a double thermo-sensitive and narrow dispersed PNIPAm110-PEO100-PPO65-PEO100-PNIPAm110 pentablock terpolymer (Scheme 1),which was synt
Strain-hardening property of polymer melts during the uniaxial extension has been extensively studied,and it induces a so-called self-healing effect which supports a homogeneous deformation of the mel
Rheological measurements are utilized to examine the yielding behavior of a polystyrene (PS) core and poly (N-isopropylacrylamide) (PNIPAM) shell microgel system with varying shell/core ratio.For a sh