The behavior of Cu-Ni-Ag-Al alloy used as anode for aluminum electrolysis was directly visualized in a two-compartment see-through cell during electrolysis, and its performances were tested at 850℃ in
【机 构】
：
School of Materials & Metallurgy,Northeastern University,Shenyang 110004,China
【出 处】
：
2004年有色金属冶金及材料第二届国际学术会议
论文部分内容阅读
The behavior of Cu-Ni-Ag-Al alloy used as anode for aluminum electrolysis was directly visualized in a two-compartment see-through cell during electrolysis, and its performances were tested at 850℃ in acidic electrolyte molten salts consisting of NaF-AlF3-8％NaCl-5％CaF2-4％Al203 for 40h in a laboratory cell. The results show that nascent oxygen oxidized the anodic surface to form oxide film at the beginning of electrolysis. Post electrolysis, X-ray diffraction analysis of alloy surface show oxide film on the anodic surface consist of CuO, NiO, A12O3, CuAl2O4 and NiAl2O4. However, SEM photo shows the oxide film is porous, loose and easy to fall into electrolyte and contaminate aluminum. The corrosion mechanism of metal anodes is analyzed in this paper.
其他文献
Nickel-sulfur electrode was obtained in a modified Watts bath by adding thiourea (TU) into the bath. The effects of TU concentration, current density, temperature and pH value of electrodepositing sol
A new type of metal matrix composite with a composition of Al2O3-33.8Fe-26.2Ni (wt.％) used as inert anode was developed in this article. Aluminum electrolysis with this anode was conducted for 12 hour
The power feeding curve of graphitized furnace is a key technique in production of the electrode. The furnace is improved in order to reduce the power consumption of the electrode, to cut short the po
In the blast furnace slag, titanium disseminates in various mineral phases(perovskite, spinel, Ti-rich diopside, Ti(C、 N) and titannaugite). Based on the technique of selective precipitation, titanium
According to the thermogravimetric analysis of cobalt oxalate, different micropowder of Co3O4 was prepared from cobalt oxalate by thermal decomposition at different condition, which was characterized
A series of the electrode materials (LiCoO2) for Lithium ion batteries were synthesized by radiating the mixture of Lithium oxide and Cobalt oxide in microwave field. The synthesizing conditions inclu
As well known, there exists a reciprocal relationshipbetween refractories industry and high temperatureindustries, in particular metallurgy industry.Refractories are consumed in many metallurgicalproc
Ni-S-Co alloy was prepared by electrodeposition in a modified Watts bath with addition of thiourea (TU) and CoCl2. The structure and morphology were determined by XRD and SEM respectively. The content
The slag non-autoclaved and unburned brick(SNAUB) was prepared on laboratory scale using the high titania BF slag (HTBFS) as aggregate, styrene-acrylate emulsion as cementing materials and two admixtu
The purified Co-Ni residue, in the process of zinc hydrometallurgy, is treated with the hydrometallurgical process. The flow sheet, which is researched by us, indicates that cobalt, nickel and cadmium