【摘 要】
:
SiO2/ZrO2-SiO2 composites were fabricated by sol-gel method, and then the flexural property of SiO2/ZrO2-SiO2 composites was discussed.The results showed th
【机 构】
:
Science and Technology on Advanced Ceramic Fibers and Composites Laboratory,National University of D
【出 处】
:
2016’中国溶胶-凝胶学术研讨会暨国际论坛
论文部分内容阅读
SiO2/ZrO2-SiO2 composites were fabricated by sol-gel method, and then the flexural property of SiO2/ZrO2-SiO2 composites was discussed.The results showed that SiO2/ZrO2-SiO2 composites were fabricated by sol-gel method.No obvious pores are existed.The SiO2 fibers are covered by ZrO2-SiO2 sol, which show a better fiber/matrix interfacial bonding.The flexural strength at room temperature is 100.8MPa, and the elastic modulus is 29.19GPa.There are mainly fibers bundles pull-out when the load reaches at the maximum.The matrix fails when the stress reaches the maximum, the samples show a typical ductile/gradual fracture behavior.After high-temperature oxidation, the fracture mechanism of the composites changed, which showed typical brittle/sudden fracture.The fracture mechanism is brittle mode.The flexural strength and elastic modulus of the samples after 1200℃ oxidation are about 50.51MPa and 31.51GPa, respectively.Compare to SiO2/SiO2 composites, SiO2/ZrO2-SiO2 composites showed higher flexural strength and higher elastic modulus.SiO2/ZrO2-SiO2 composites, which fabricated by sol-gel method, show long time usage at higher temperature.
其他文献
体育教学是学校体育教师按照一定的计划,通过教师的教和学生的学进行的教学过程,目的是让学生科学掌握锻炼身体的方法,提高学生的运动技能,从而增强体质,培养意志,甚至在比赛
商界巨头进军足球,企业家是怎么想的?这是一种单纯的品牌增值,还是一种多元化布局影响指数★★★热门事件:2016年,体育产业步入高速增长期。10月份,发改委印发了《中国足球长
针对无人车辆四轮独立转向过程中因不同步而产生的轮胎拖拽问题,设计了四轮独立转向系统电气式同步控制方案,建立了Simulink模型并进行了仿真分析.仿真结果表明:在给两个转向
根据复合悬挂的数学模型在RecurDyn中建立了半车动力学模型,仿真研究了扭杆工作直径和阻尼匹配对整车加速度均方根值的影响.在此基础上,对比研究了6种复合悬挂匹配方案对某型
In this paper,polyethylene glycol (PEG) /polyvinyl alcohol (PVA) composite hydrogel filmswere prepared by blending (PEG) and PVAof different molecular weigh
社会经济的快速发展,在一定程度上造成了环境污染,使得环境问题愈发突出,成为近年来社会各界广泛关注的问题之一.石漠化是一种非常独特的生态环境问题,成因较为复杂,并且由于
采用细观离散元法,通过土壤参数试验、履带板土槽试验及EDEM和RecurDyn协同仿真,对履带车辆与地面相互作用关系进行了分析,得到了履带车辆转向阻力(包括剪切阻力、摩擦阻力、
Silk fibroin is a kind of natural polymer biomedical material with good biocompatibility and biodegradability.In this paper, Na2CO3 solution was used to deg
一所农村高中,师资不占优势.而地理学科的高考成绩这几年能在全市同类学校中脱颖而出,得益于我校“团队引领、和谐兴校”理念的指引,更得益于我们地理组着力打造一支和谐的教
Tantalum carbide (TaC), hafnium carbide (HfC) and compounds in the Ta-Hf-C system have extremely high melting points (> 3700 ℃) making them potential candi