Formation of Abrasive Superhard COMPOSITE Materials Basrd on Diamond and Cubic Boron Nitride Structu

来源 :第二届中国国际复合材料科技大会 (CCCM-2) | 被引量 : 0次 | 上传用户:bhf0520
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
  The results of work on the development of abrasive superhard composite materials based on diamond and cubic boron nitride due to structuring the powder material by carbon binder at subatmospheric pressures are presented in the paper.
其他文献
Carbon nanotube (CNT)-reinforced copper composite was fabricated by hot pressing for CNTs-embedded copper composite particles, which involves solution phase synthesis of CNTs-implanted cuprous oxide c
会议
The pre-oxidized SiO2 layer and salt-bath plating Ti5Si3 coating layer were developed on the surface of SiCP.Effects of surface states on the microstructures and tensile properties of 2vol.% SiCP/2014
In this study, a partial graphitic hierarchical porous carbon nanofiber (PGHPCNF) is prepared via eletrospinning followed by pyrolysis, KOH activation and acid treatment.The as-obtained carbon nanofib
A high-yield porous graphene/carbon nanowire (PG/CNW) composite is synthesized via in-situ chemical oxidative polymerization followed by carbonization and KOH activation.An easy and efficient vacuum-a
Glass transition temperature (Tg) of epoxy resin composites reinforced by amino groups (-NH2) and carboxyl groups (-COOH) grafted carbon nanotubes (CNTs) were investigated, respectively, and compared
A novel magnetic multi walled carbon nanotubes with fluorescent imaging performance (F&M-MWCNTs) was successfully fabricated by combining in situ atom transfer radical polymerization (ATRP) and fluore
The eco-friendly and renewable polymers (poly(dopamine) and hydroxyethyl cellulose) were used as modifiers to enhance dispersibility of short carbon fibers (SCFs) in water-based solution.The dispersio
In this study, AZ31B magnesium alloy was treated by different kinds of silanes, including γ-(2,3-epoxypropoxy) propyltrimethoxysilane (KH-560), γ-(methacryloxy) propyltrimethoxysilane (KH-570), N-(2-a
Aluminoborosilicate glasses with different CaO/La2O3 ratio were prepared by conventional melt quenching method.The structure were investigated by FTIR.The thermal property was always measured by DSC.T
An active composite is a type of an active material without the usage of any functional material such as shape memory alloy or piezoelectric material, but its shape can be changed during the thermal a