Preparation and dielectric properties Barium strontium titanate niobate composite ceramics by powder

来源 :2012 Postdoctoral Symposium of China on Materials Science & | 被引量 : 0次 | 上传用户:yanqingqing1213
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
  Barium strontium titanate niobate (BST/SBN) composite ceramics system following the general formula 0.7BaO·0.3SrO·(1-y)TiO2·yNb2O5 were firstly prepared by the modified Powder-Sol method.By controlling the viscosity of the sol solution, Nb2O5 powders was uniformly suspended in the BST Sol.Powders obtained from dried gels were calcined at 800℃ for 3h.The samples were prepared at a pressure of 300MPa from dried powders.The bulk samples were sintered at 1200℃for 3 h.The results of the XRD indicate that the perovskite phase and the tungsten bronze phase coexisted stably in BST/SBN.The relative dielectric constants (εr) and dielectric loss (tang) of 0.3SrO·0.7BaO·yNb2O5·(1-y)TiO2 are improved when the values of y is 0.4~0.6.
其他文献
As excellent inorganic electrochromic materials, tungsten oxide films have enormous potential applications in transportation, energy fields.However, the electrochromic time needs to be shortened and t
0.3SrO·0.7BaO·yNb2O5·(1-y)TiO2 composite ceramics with different Nb/Ti ratios were, for the first time, fabricated using a Powder-Sol (P-S) method with Nb2O5 fine powders suspended in the barium stron
通过等离子合金化技术在不锈钢表面制备TiN薄膜,然后对TiN薄膜进行热氧化得到N掺杂TiO2薄膜.同时制备TiO2薄膜作为对比研究.利用X射线衍射(XRD)、X射线光电子能谱(XPS)、扫描电子显微镜(SEM)及紫外-可见分光光度仪(UV-Vis)对得到的薄膜进行表征.XRD测试结果表明:经过450℃氧化处理的薄膜中存在锐钛矿晶型的TiO2.经热氧化后薄膜表面均匀分布着尺寸接近的微小凸起物.TiO
熔体法生长的半绝缘碲锌镉(Cd1-xZnxTe或者CZT)晶体中存在着很多缺陷,这些缺陷作为陷获中心在带隙中引入了深能级,从而严重影响CZT的探测性能.分别采用初始上升法和同步多峰分析法(SIMPA)分析热激电流谱(TSC),从而获得了半绝缘的铟掺杂的Cd0.9Zn0.1Te晶体中的陷阱能级分布.结果表明:由丁重叠峰的干扰,初始上升法在确定陷阱峰的最大值时会产生较大的误差;而SIMPA法被证实适用
The residual stress of silicon-doped CVD diamond films with various SiC/C ratios are evaluated using both X-ray diffraction analysis and Raman spectroscopy measurements.The examined Si-doped diamond f
The excellent chemical and mechanical properties of SiC single crystal make damage free surface preparation for SiC wafers a great challenge.Double side lapping, mechanical polishing and chemical mech
The microstructure, tensile properties and fractography of A356 aluminum alloy with As-cast and T6 conditions obtained using expendable pattern shell casting process were investigated.The results show
The influences of aging time and aging temperature on the microstructure and mechanical properties are investigated on the 6005A aluminum alloy extrusions.Artificial aging is performed on the alloy ex
In hot stamping operations the influence of process parameters on the properties of final part is fundamental in the design and optimisation of the forming process.Hot stamping process parameters were
In order to further enhance the TiO2 photocatalyst activeness, this research uses the non-metallic ion doping to modify TiO2.In this study, selected nonmetal B has prepared the doping modification TiO