A Co3O4/RGO/Co3O4(CRC)pseudocomposite on cobalt foil was prepared through a one-pot in-situ hydrothermal method.Based on the chemical redox reaction between
【机 构】
：
Key Laboratory for Ultrafine Materials of Ministry of Education,Shanghai Key Laboratory of Advanced
论文部分内容阅读
A Co3O4/RGO/Co3O4(CRC)pseudocomposite on cobalt foil was prepared through a one-pot in-situ hydrothermal method.Based on the chemical redox reaction between Co foil and graphene oxide(GO),and the electrostatic attraction between GO(negative charge)and Co2+(positive charge),a novel sandwich structure,Co3O4(from Co2+ions),RGO,Co3O4(from Co foil),was designed and constructed.The Co3O4/RGO/Co3O4(CRC)@Co nanocomposite was directly utilized as a binder-free supercapacitor electrode,and the CRC@Co composite prepared at 200 °C for 24 h exhibited superior electrochemical performances: capacity specific capacitance of 2272.7 mF cm-2 at 5 mA cm-2,and a capacity retention of 81.6%even after 2000 charge-discharge cycles.
其他文献
本文采用原位还原法,在NaBH4还原的石墨烯片层(RGO)上原位生长金纳米粒子,并用该复合物催化有机污染物对硝基苯酚(4-NP)的还原反应.该法制备过程中未添加其他还原剂和表
单纳米线太阳能电池，由于天线效应和光生载流子可以高效地分离，吸引了大量的关注。然而，对于这种新出现的光伏器件，光学和电学的性能距离期望值还很远，所以研究者们渴望找到更
常被用于解决析氢反应动力学缓慢的铂基催化剂由于其高成本以及稀缺极大的阻碍了限制氢能的发展。所以发展低成本的非贵金属催化剂对氢能的发展显得至关重要的。本文报道
用低温液相法先合成准单分散的较大尺寸氧化亚铜微米球，通过对氧化亚铜的高温氧化，得到准单分散的氧化铜微球。对氧化亚铜及氧化铜分别进行氧化石墨烯的包覆并用作锂离子电
设计合成了一系列羧基功能化离子液体，通过调控该离子液体的碳链长度，该类离子液体在碳酸丙烯酯中溶解度可随着温度的变化而改变。我们通过核磁和DFT理论模拟等手段发现，其
目前,一系列的离子液体被发现可以溶解纤维素,随之而来也有了许多机理研究,但都缺乏原子层面的理解。针对此问题,我们建立了符合真实结构的纤维素微丝,放在水、[Emim]OAc
离子液体作为一种绿色溶剂,在溶解天然高分子方面表现出良好的溶解性能.以离子液体为溶剂溶解羊毛角蛋白也受到了越来越多的关注.但是,具有不同阴、阳离子结构的离子液体
将氮掺杂石墨化碳层(NGC)引入铂碳催化剂(Pt/C)表面,制备了一种具有高稳定性和双催化活性位点的Pt/C@NGC核@壳结构催化剂.采用循环伏安加速寿命实验,结合LSV、TEM和XPS考
为研究载体对甲酸盐电氧化催化剂抗毒性的促进作用,将商用催化剂Pt/C 和Pd/C 分别与石墨烯(GNs)及掺N 石墨烯(NGNs)超声混合后涂制电极,通过循环伏安法(CV)及计时电流法(