Tb3+ and Yb3+ codoped Lu2O3 nanophosphors were synthesized by the reverse-strike co-precipitation method.The obtained Lu2O3:Tb3+, Yb3+ nanophosphors were characterized by X-ray diffraction (XRD) and p
【机 构】
:
Department of Physics, University of Science and Technology of China, Hefei 230026, P R China;Colleg
论文部分内容阅读
Tb3+ and Yb3+ codoped Lu2O3 nanophosphors were synthesized by the reverse-strike co-precipitation method.The obtained Lu2O3:Tb3+, Yb3+ nanophosphors were characterized by X-ray diffraction (XRD) and photoluminescence(PL) spectra.The XRD results show that all the prepared nanophosphors can be readily indexed to pure cubic phase of Lu2O3 and indicates good crystallinity.The Tb3+→yb3+energy transfer mechanisms in the UV-blue region in Lu2O3 nanophosphors were investigated.
其他文献
Effect of Ce3+ ions introduction on 2 μrm emission properties and energy transfer mechanism in Yb3+/Ho3+-doped fluorophosphate glass has been investigated.From the measured fluorescence spectra, stron
近年来随着半导体照明技术的飞快发展,用于白光LED的稀土掺杂荧光粉的发展异常活跃,其中Ce3+掺杂的YAG黄色荧光粉获得了商业应用.Ce3+由于具有相对较快(~20-40 ns)的5d-4f允许宽谱跃迁发射,是闪烁体材料和照明、显色用发光材料的理想掺杂剂.例如Ce3+掺杂的LaBr3,Lul3闪烁体材料及YAG,CaAlSiN3白光LED用荧光粉具有接近100%的量子产率.但是在稀土倍半氧化物R2
The thermal stablility and 2 μm emission properties of Yb-Tm-Ho triply-doped silicate glass are investigated.The characteristic temperatures, absorption spectrum and fluorescence spectrum of the glass
2.7 μm emission properties and energy transfer mechanism of Nd3+/Er3+ co-doped sodium tellurite glasses were investigated in present paper.Absorption and emission spectra were tested to characterize t
A detailed characterization of structural analysis and energy transfer (ET) process in Tm3+ doped germanate glasses has been presented.The thermal stability and Raman spectroscopic analysis of the hos
A series phosphors of Ca2SiO4:RE (RE=Sm3+, Dy3+) were prepared by the solid-state reaction method.The influence of annealing temperature, RE-dopant concentration and Li+,Na+ ions charge compensation o
铋掺杂玻璃能够发射覆盖1000~1600 nm波长范围的超宽带红外发光,荧光最大半高宽(FWHM)约300 nm,其独特的超宽带光学性能预示着它很有希望成为新型超宽带光放大材料.但目前为止,铋掺杂玻璃的红外发光机理仍不明确,铋掺杂玻璃在980 nm波长泵浦下已实现宽带荧光发射和光放大,但吸收截面较小,泵浦效率较低.本文工作中,制备了组成为(70-x)SiO2-xLa2O3-30CaO-1.5Bi2
当LiGdF4:Eu材料被首次报道在真空紫外激发后其量子效应可达到200%,量子剪裁材料就成为了一个热门的研究方向.高效率的下转换通常是基于量子剪裁荧光材料可以在每一次吸收高能量的光子之后产生两个低能量光子的原理实现的.而最近发现近红外区的量子剪裁荧光材料有可能提高以Si为衬底的太阳能电池的能量转换效率.将紫外线或者蓝光进行裁剪而得到的两个近红外区低能量光子很容易被太阳能电池吸收.因此,寻找一对能
稀土离子能级丰富。通过在不同的基质材料中掺杂不同稀土离子或其组合,可以获得丰富的上转换发射光谱。稀土离子这些独特的特性,使稀土掺杂材料在全固态短波长激光器、生物信息标识、太阳能电池敏化材料、发光显示材料中具有广泛的应用价值。利用简单的水热法,我们合成了yb3+-Tm3+,yb3+-Ho3+和yb3+-Tm3+-Ho3+共掺杂的NaYF4微米晶样品。在980 nm近红外光的激发下,通过对比相同激发条
基于前期对CaMoO4:yb3+红外下转换粉末材料研究的基础上,我们对材料进行不同的电荷补偿,即(1)掺杂碱土金属离子M+,通过2Ca2+→ Yb3++ M+,M+为Li+,Na+,K+实现电荷平衡;(2)间接电荷补偿即3Ca2+→2Yb3+空穴来实现电荷的匹配,获得了进一步非常有意义的结果:与未进行电荷补偿的样品相比,在266nm激发下,适当的电荷补偿使CaMoO4:yb3+粉末材料的下转换效率