The purpose of the study is to introduce a new perspective of the surface roughness measurement to explain the wetting behavior of the complex textile surfaces.
【机 构】
:
Department of Clothing & Textiles, Seoul National University, Seoul, Korea
【出 处】
:
The 12th Asian Textile Conference (第12届亚洲纺织会议暨2013年纺织学术年会)
论文部分内容阅读
The purpose of the study is to introduce a new perspective of the surface roughness measurement to explain the wetting behavior of the complex textile surfaces.
其他文献
Due to the regular molecular structure as well as the high-degree crystallinity and orientation of conventional polyester fibers, the dyeing of polyester fibers primarily conducts at high temperature
In this paper, use combed cotton yarns as a comparative sample and test four kinds of cotton-like polyester yarns morphology and tensile fracture, moisture absorption, water absorption, heat shrinkage
In this paper, PANI conductive fabrics were prepared via ultrasonic radiation and in situ polymerization of aniline on polyester, which was preprocessed by alkali weight reduction.
Phosphorus-containing copolyester fiber is currently being applied in many fields for its outstanding flame retardancy.However, a wider application has been restricted by its serious melt dripping iss
A [3-(Methacryloyloxy)propyl]trimethoxysilane (MAPTMS) modified titania hydrosol was prepared to enhance the light fastness of PET fabric.Its gel was characterized by FT-IR and XRF.
The application of polystyrene (PS) material, with its characteristic of extremely low thermal insulation similar to air and the low cost, has been limited due to its poor mechanical strength.
One dimensional PANI/TiO2 composite has been successfully synthesized by simple polymerization method.Scanning electron microscopy, transmission electron microscopy, X-ray diffraction, FTIR spectra, U
The objective of our study was to develop a new class of Fe3O4 nanocrystals decorated CNFs with characteristic porous morphology by straightforward approach.
Zn meso-tetra(4-carboxyphenyl) porphyrin anchored titanate nanotubes were synthesized with hydrothermal treatment of ZnTCPP-TiO2 gel and its properties of photo-generated holes and electrons were stud
In this article, The Ⅰ-Ⅴ characteristics of the individual Pedot nanotubes with the diameter of 92 nm, 95 nm and 160 nm were measured by an applied voltage with an interval of 0.03 V using a Physical