本文阐述了天津鞍钢天铁冷轧薄板有限公司连退线炉内带钢发生硌印的原因分析及改进的措施.通过分析和改进后消除硌印,提高了产品合格率,保障生产的顺利进行.
退火炉内带钢硌印产生原因分析及改进
【摘 要】
：
本文阐述了天津鞍钢天铁冷轧薄板有限公司连退线炉内带钢发生硌印的原因分析及改进的措施.通过分析和改进后消除硌印,提高了产品合格率,保障生产的顺利进行.
【机 构】
：
天津鞍钢天铁冷轧薄板有限公司
【出 处】
：
2016年冶金节能新技术与能源循环利用研讨会
【发表日期】
：
2016年6期
其他文献
通过一步水热处理法制备了碳量子点修饰的P25型TiO2二元复合物(CQDs/P25).CQDs/P25在紫外光和可见光下相比于纯P25均表现出更好的光催化产氢性能.通过瞬态光电流、表面光电压谱等表征手段,提出了一种新的双重作用机制,即碳量子点在紫外光区可作为电子给体接受TiO2的光生电子,而在可见光下可作为电子受体将自身激发产生的光电子传递给TiO2导带,从而使二元复合物的光催化活性得以提升.
Low-crystalline FeOOH Nanoparticle Anode with High Comprehensive Electrochemical Performance for Adv
Carbon materials are generally preferred as anodes in supercapacitors,however their low capacitance limits the attained energy density of hybrid and asymmetric supercapacitors.Here,we develop a novel
In-situ growth of Ni2P nanoparticles on Hierarchical Porous Graphitic Carbon as super stable anode m
Sodium-ion batteries have recently gained a lot of interest due to its low cost and widely applications.However,the main challenge is to develop an anode material with superior high-rate capability an
用低温液相法先合成准单分散的较大尺寸氧化亚铜微米球,通过对氧化亚铜的高温氧化,得到准单分散的氧化铜微球.对氧化亚铜及氧化铜分别进行氧化石墨烯的包覆并用作锂离子电池电极材料,发现经过包覆后的材料在比容量及循环稳定性方面都有较大的提升.在首次放电过程中,氧化石墨烯发生了原位的电化学还原,形成新的石墨烯三维导电网络而不会再被电化学氧化.包覆结构及三维导电网络的构建有利于比容量及循环稳定性的提升,也说明了
Nanoconfined Carbon-Coated Na3V2(PO4)3 Particles in Mesoporous Carbon Enabling Ultra Long Cycle Life
Na3V2(PO4)3(denoted as NVP)has been considered as a promising cathode material for room temperature sodium ion batteries(NIB).Nevertheless,NVP suffers from poor rate capability resulting from the low
离子液体作为一种绿色溶剂,在溶解天然高分子方面表现出良好的溶解性能.以离子液体为溶剂溶解羊毛角蛋白也受到了越来越多的关注.但是,具有不同阴、阳离子结构的离子液体对羊毛角蛋白溶解能力不同,这一过程的机理研究仍是一个巨大的挑战.本研究设计合成了一系列1,5-二氮杂双环[4.3.0]-5-壬烯类离子液体,将其应用于羊毛角蛋白的溶解,并对离子液体结构对羊毛角蛋白溶解性能的影响进行了系统的研究,发现阴、阳离
3D Hollow Sphere Co3O4/MnO2-CNTs:Its High-performance Bifunctional Cathode catalysis and Application
Recently,there has been a continuous requirement for high active,excellently durable,and low-cost electrocatalysts for rechargeable zinc air battery.Among many low-cost metal based candidates,transiti
MoO2@C nanoflowers were synthesized through a grinding method,followed by an annealing process.With excellent dispersity and structural integrity,the obtained MoO2@C dilivers a reversible capacity of
会议
The template-free synthesis of hierarchically porous anatase TiO2 via acid-etching for enhancing the
Although anatase TiO2 has good performances in many applications,it is very difficult to synthesize nanocrystalline anatase TiO2 with high specific surface areas.Herein,a two-dimensional hierarchicall
会议
Preparation and characterization of cross-linked polybenzimidazole/quaternized poly(1-vinylimidazole
An anion exchange polymer(QPVI-75%)has been synthesized via the quaternization reaction of poly(1-vinylimidazole)with 1-bromohexane.A series of cross-linked blend anion exchange membranes have been su