Structural steels with yield strength requirements greater or equal to 690 MPa can be produced through controlled recrystallization hot rolling coupled with precipitation strengthening or purposeful heat treatment through quench and tempering(Q&T).High strength structural steel and wear/abrasion resistant requirements greater or equal to 360 Brinell hardness(BHN)are produced by the development of microstructures of tempered lower bainite and/or martensite through the Q&T process.While these Q&T microstructures can produce very high strengths and hardness levels making them ideal for 690 MPa plus yield strength or wear/abrasion resistant applications,they lack toughness/ductility and hence are very brittle and prone to cracking.While tempering the microstructures helps in improving the toughness/ductility and reducing the brittleness,strength and hardness can be sacrificed.In addition,these steels typically consist of alloy designs containing boron with carbon equivalents(CE)greater than 0.50 to achieve the desired microstructures.The higher CE has a negative influence on weldability.