Magnetocaloric Effect around the First-to-Second Order Phase Transformation of La0.7Ca0.275Ba0.025Mn

来源 :第八届国际稀土开发与应用研讨会暨第三届中国稀土峰会 | 被引量 : 0次 | 上传用户:boge66
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
  In this work,we present a detailed study on the magnetocaloric effect of the first-to-second order magnetic phase transformation of La0.7Ca0.275Ba0.025MnO3 nanocrystals with averaged crystallite size about 38-200 nm.
其他文献
By controlling Dy vapor deposition process,the amount of Dy diffused into the magnet was increased gradually from 0.1 wt.%to 0.3 wt.%.
A series of luminescent emission-tunable phosphors Ca12Al14O32F2:Tb3+,Eu2+,Eu3+have been synthesized by a high temperature solid-state reaction in a reductive atmosphere.The sample phase was determine
As the major ingredient of natural gas,methane induced Greenhouse Effect is almost 20 times more serious than CO2.
Low saturation magnetization limits the enhancement of the properties of Sm-Co system and thus their broad application in high temperature area.
Zeolite Y is widely used in catalysis,adsorption,ion exchange and other fields,which has many unique properties because of its uniform and regular pore structure,enormous surface areas and more surfac
Due to its excellent UV-rays shielding properties,size-controlled ceria nanoparticles were prepared by chemical method.Then the surface of nanoparticles was modified by surfactant and were embedding i
Hydrogen storage alloys La0.83-xSmxMg0.17Ni3.1Co0.3Al0.1(x = 0.0-0.4)were prepared by induction melting followed by annealing treatment in argon atmosphere.
Solid oxide fuel cells are of great interest because they are composed of all-solid components and elevated operating temperatures,providing superior performance such as fuel utilization efficiency,du
A novel yellow emitting long lasting phosphate phosphor Ca6BaP4O17∶Eu2+,R3+is developed.
A large amount of wastewater generated in flotation process of phosphate ore has to be treated before returning to flotation operation.