【摘 要】
：
2D Carbon fiber reinforced silicon carbide matrix composites (2D-C/SiC) preformed by carbon cloths were fabricated by chemical vapor infiltration (CVI).The
【出 处】
：
第二届中国国际复合材料科技大会 (CCCM-2)
论文部分内容阅读
2D Carbon fiber reinforced silicon carbide matrix composites (2D-C/SiC) preformed by carbon cloths were fabricated by chemical vapor infiltration (CVI).The thermal diffusivity and specific heat capacity of 2D-C/SiC were t l ested from RT to 1200 ℃.The results shows that the specific heat capacity is increased with increasing of the temperature at the beginning, it reaches the maximum value of 1.6J / (g·K) at 1000 ℃, and then it keeps nearly constant by 1200 ℃.On the contrary, the thermal diffusivity of 2D-C/SiC is decreased with increasing of the temperature.It is 13.45mm2/s at RT, and it reduces to 6.14mm2/s at 1200℃.
其他文献
随着微电子技术的不断发展，单位面积电子元器件散热量不断增加。为了保证电子元器件正常工作及稳定，需尽快把热量散发出去。高性能的电子封装材料是有效解决散热问题的重要
随着微电子技术及集成电路的快速发展，器件散热量急剧增加，金刚石颗粒分散铝基(铝/金刚石)复合材料成为应用前景广阔的新一代热管理材料。然而，铝/金刚石界面处形成的碳化铝
本研究对粉末冶金法制备的17％voi.SiCp/2009Al复合材料进行热压缩试验,采用改进的动态材料模型绘制加工图,同时计算出流动应力的温度敏感指数s值分布图,并结合微观组织观
采用单向拉伸与压缩实验研究了真空热轧复合06Cr19Ni10/Q235层状复合材料室温力学性能与变形协调性，并研究不同条件(覆层比例、变形速率、变形率、复合界面与载荷方向夹角
对于硼化物强化镁锂基复合材料，改善复合材料性能除了改变增强相的分布和数量外，强化基体也是有效方法，基于对复合材料中增强相的分布和数量的研究，针对复合材料性能仍不能满
采用旋转摩擦挤压法(Rotational friction extrusion,RFE)制备多壁碳纳米管增强铝基(CNTs/Al)复合材料,并对CNTs/Al复合材料的显微组织、硬度和磨损性能进行分析。结果
采用磁控溅射法在金刚石(Diamond)颗粒表面成功制备了金属钼(Mo)涂层,对磁控溅射后金刚石颗粒进行后续热处理,分析了热处理前后Mo涂层的成分和形貌；采用气压浸渗法制备Dia
为了研究碳化硅颗粒(SiCp)尺寸和体积分数对中体积分数SiCp增强铝基复合材料的导热系数的影响,用粉末冶金工艺制备体积分数为30、35和40 vol％,颗粒尺寸为3、8、15、25和40
The Al2O3 fibers/Al2O3 composite was prepared using homogeneous reinforcement technology, and the properties was studied.Firstly, the Al2O3 fibers were obta
Microwave technique was applied to sinter polymer derived silicon carbide.In order to figure out the crystallization behavior of SiC, microwave technique an