【摘 要】
：
Effects of Y2O3 addition on the microstructure and electrical properties of the SnO2-based varistor system were investigated.It was found that Y2O3 helps to
【机 构】
：
Key Laboratory of Functional Materials and Devices for Special Environments of CAS
【出 处】
：
第十四届全国敏感元件与传感器学术会议
论文部分内容阅读
Effects of Y2O3 addition on the microstructure and electrical properties of the SnO2-based varistor system were investigated.It was found that Y2O3 helps to greatly reduce the averaged grain size and improve the electrical properties of SnO2-based ceramics.The nonlinear coefficient (t =22.0) of the sample and the break-down electrical field (1105.8 V/mm) were obtained with the addition of 0.50 mol% Y2O3.The relative dielectric constant (at 1kHz)decreases from 4233.6 to 1350.2 with the increase of the Y2O3 content.
其他文献
氧化铟锡(ITO)是一种n型简并半导体材料ITO薄膜作为一种透明导电薄膜被广泛应用于LCD领域,同时也可以作为一种高温薄膜热电偶电极材料.本文采用射频溅射的方法在取向为(100)
井下煤矿瓦斯泄漏是引发重大矿难事故的主要原因.为应对现有技术在安全性及可靠性方面的瓶颈问题,结合笼形超分子穴番敏感膜材料,本文研制了一种采用SiO2/36°YX LiTaO3声波
本文报道了一种将TiO2与还原氧化石墨烯(rGO)复合,制备出具有桥接结构的新型复合材料的气敏响应特性研究.利用溶胶-凝胶法制备了TiO2前驱体,在TiO2和氧化石墨烯复合的过程中
SnO2和ZnO作为两种种重要的n型半导体氧化物传感材料,基于其制成的敏感元件由于具有好的气敏特性的以及稳定性从而被广泛的应用在生产和生活中.近年来,很多研究表明构筑ZnO/S
高温下仍能保持低电阻率、高可靠性的金属引线电极是抗恶劣环境的MEMS压力传感器芯体的重要组成部分.高温环境金属电极层与层之间的相互反应和扩散会导致电极电阻率升高甚至
本文通过喷涂沉积的方法制备出了基于P3HT/C61异质结薄膜的有机薄膜晶体管二氧化氮(NO2)气体传感器的有源层.并对该传感器的电学特性和气敏性能进行了测试.此外,本文通过扫描
本文采用静电纺丝方法制备出了Ni3Sn4纳米颗粒负载的碳纳米纤维材料.通过FESEM可看出,材料由纳米颗粒负载的纳米纤维组成.通过对其进行EDS分析,颗粒的主要成分为Ni和Sn元素,
本论文制备基于In2O3/石墨烯复合材料的气体传感器,石墨烯具有超大比表面积、超高的电子迁移率等优点,与In2O3复合后有望进一步提高气敏特性,实现对有毒有害气体高效快速的检
结合光晶体管和有机半导体的优势，制备了基于CuPc单晶微/纳米带有机场效应晶体管,通过光照强度和栅极电压以及源漏电压的控制可以实现快速响应的光电开关,显示了在有机光电子
In this paper, reduced graphene oxide (RGO) thin film were prepared by spin-coating method to detect NO2 gas at different temperatures.Results showed that t