【摘 要】
：
TGG polycrystalline and TGG monocrystal belong to cubic system.TGG polycrystalline is composed of many single crystal grains and boundary layers.TGG polycrystal and monocrystal are with the similar st
【机 构】
：
Engineering Research Center of Photoelectric Funcional Materials of Ministry of Education,Changchun
【出 处】
：
第17届全国晶体生长与材料学术会议
论文部分内容阅读
TGG polycrystalline and TGG monocrystal belong to cubic system.TGG polycrystalline is composed of many single crystal grains and boundary layers.TGG polycrystal and monocrystal are with the similar structures and physical performance,and both have high Verdet constants that are V=36.4 rad/Tm,V=36.2rad/Tm,respectively,which are within 36-40 rad/Tm.
其他文献
[011]取向弛豫铁电单晶具有较高的压电常数(d33)和机械品质因子(Qm)，因而在医用超声换能及外科手术器件等领域具有广阔的应用前景。[1]然而准同型相界(MPB)附近[011]取向的单晶极化后容易诱导形成近单畴的正交(O)相，压电常数大大降低。
溴化钾晶体是具有高透过、低吸收和光学均匀性高的典型碱金属卤化物。随着科学技术的发展，国内外对红外光谱仪需求越来越广泛，则对优质大尺寸溴化钾窗片需要也逐渐上升。
采用提拉法生长Ca2Al2SiO7(CAS)晶体,使用排水法测得晶体密度为3.059g·cm-3,XRF分析发现各组分有效分凝系数接近于1,不同生长阶段的晶体组分均匀,HRXRD结果表明CAS晶体结晶质量良好.
氟化镁(分子式：MgF2)晶体在紫外、可见和近红外波段具有良好的透过性能、荧光辐射小、双折射等性能，是紫外光电探测器、紫外激光器和紫外光学系统的理想材料。
季戊四醇(PET)是重要的X射线分光晶体,是X 射线光谱仪、电子探针谱仪和X 射线荧光光谱仪的核心元件材料之一。从溶解度性质看,PET晶体可采用水溶液降温法生长,但其水溶液稳定性差,晶体难以正常生长。
利用提拉法生长出高质量的Yb：GdYCOB晶体，测试了晶体的在较高温度下的压电性能，并研究Yb与Gd不同掺杂比例对晶体的高温压电性能的影响，分析其产生的原因。
本文采用高温熔体拉法生长得到一种新型硅酸镓镧类晶体Sr3TaAl1.5Ga1.5Si2O14(STAGS)，并对所制得晶体的物相、结晶质量、组分、压电系数、高温电阻率、透过率开展了研究.
一定强度的电场作用下，弛豫铁电单晶中可以诱导出铁电—铁电相变，且诱导相变电场强度因晶体的组分和取向的不同而不同[1-2].Shrout等人认为，电场诱导的相变是引起PZN-PT单晶大电致应变的原因[3].
采用坩埚下降法生长出稀土掺杂Bi4Si3O12晶体,掺杂元素包括Sm、Eu、Gd、Tb、Dy、Ho、Tm、Yb等,晶体尺寸为Φ25mm,晶体透明但原生态晶体表面有少量富Bi析出物。
利用X射线全散射数据进行对分布函数分析,可以获得在水热条件下合成纳米锐钛矿TiO2形核与生长机制,以及纳米颗粒结构缺陷的相关信息。研究发现,反应物先驱体可以用Ti的氢氧化物簇来描述,这种Ti的氢氧化物簇由几个TiO6/TiO5单元组成,排列方式与锐钛矿结构相似。另一方面,水热条件下纳米材料的形成与长大机制既不同于常温溶液下单分散溶质的析出过程,也不同于高温固态反应的结晶过程。进一步研究发现,当Ti