【摘 要】
：
In this paper, the performance of JHMGC 100S, a kind of HDPE for pipe, was studied, and the comparison with other typical PE 100 resin at home and abroad was also did.The results show that: the impact
【机 构】
：
Daqing Petrochemical Research Center, Hei Longjiang, Daqing, 163714 China
【出 处】
：
Asian Polyolefin Workshop (APO2013)2013亚洲聚烯烃研讨会
论文部分内容阅读
In this paper, the performance of JHMGC 100S, a kind of HDPE for pipe, was studied, and the comparison with other typical PE 100 resin at home and abroad was also did.The results show that: the impact strength of JHMGC100S was higher than other samples, and the bending strength was almost the same;the molecular weight distribution was obvious bimodal;the processability of JHMGC 100S was good, and the hydrostatic strength of the pipe which was produced by JHMGC 100S fulfilled the rule in GB 15558.1-2003.
其他文献
Isotactic polybutene-1 (iPB) was first prepared by Natta and coworkers in 1954[1].iPB was a special semicrystalline thermoplastic polyolefin with some attractive mechanical properties such as excellen
Heterogeneous silica-supported systems, such as Phillips or Union Carbide catalysts, have been widely used in the large scale industrial production of polyolefins.1-2The ill-defined nature of these ca
Half-metallocene-type of group 4 complexes have attracted considerable attention not only in the field of catalysis, organometallic chemistry, but also in the field of polymer chemistry due to their u
We have recently developed advanced THC catalyst which is improved stereoregularity in propylene polymerization as well as copolymerization activity for ethylene-propylene copolymerization compared wi
The chain microstructure, crystallization and morphology of three olefinic blocky copolymers (OBCs)1 were compared.Analysis of the 13C NMR spectra with two-site first-order Markovian model2 reveals th
Polypropylene (PP) is one of the most versatile thermoplastics, due to its well-balanced mechanical properties, easy processability, lightweight, low environmental load, and so on.1 Numerous studies h
The cycloolefin polymers (COPs) have attracted much attention due to their fascinating properties, such as high transparency, low water absorption, chemical resistance and so on.
Since chromium catalyst was firstly discovered in 1953[1,2], it can be divided into three kinds, which are Phillips catalyst, chromocene catalyst and organo-chromate catalyst[4].
Heterophasic copolymers of polypropylene (PP) containing dispersed ethylene-propylene random copolymers (EPR), known as impact PP copolymers (IPC), are an important sub-class of PP that are superior t
Copolymerization of 1,3-butadiene with (E)-l-phenyl-1,3-butadiene (1PB) was investigated in a large range of 1PB feed ratios (0～50 mol％) by using CpTiCl3/MAO catalyst.