Accelerated stress tests (ASTs) were performed to study the degradation mechanism of PTFE reinforced perfluorinated sulfonic acid (PFSA) ionomer with intensive humidity cycles and load cycles.It was recognized that the edge of membrane & electrode assembly (MEA) should be carefully treated to prevent the immediate failure for excessive or non-uniform mechanical stress caused by frequent humidity changes.