【摘 要】
:
Stress corrosion cracking(SCC)is a common type of equipment failure in chemical industry,especially for stainless steels equipment.However,many end users are not familiar with this failure mode when i
【机 构】
:
DuPont China Holding Co.,399 Keyuan Road,Shanghai,China
【出 处】
:
国际腐蚀工程大会(ICEC2016)
论文部分内容阅读
Stress corrosion cracking(SCC)is a common type of equipment failure in chemical industry,especially for stainless steels equipment.However,many end users are not familiar with this failure mode when it happens to their stainless steel equipment.
其他文献
In this paper we show that screws made of mild steel can,in principle,be electrochemically coated with up to 20-μm-thick amorphous Al-Mn coatings in an ionic liquid composed of MnCl2-AlCl3-1-ethyl-3-m
Six science journals are published in the Institute of Metal Reasarch,Chinese Academy of Sciences(IMRCAS).In this reports,we introduce the history and current development of these journals in IMR,putt
1.Engineering application environment: Sanshan island which located in the South Bank of Bohai Bay(Shandong),is a small peninsula surrounded by water on three sides.
Localized corrosion behavior of Q235 steel in seawater containing sulphate-reducing bacteria(SRB)is investigated by wire beam electrode(WBE)technique,electrochemical measurement method and surface ana
Certain species of sulfate-reducing bacteria(SRB)use cathodes as electron donors for metabolism,and this electron transfer process may influence the proper protection potential choice for structures.
Surface and interfacial chemistry plays a critical role in developing advanced anti-corrosion systems,and the key to the successful coating system is the initial formation of a chemical conversion fil
The microbiologically influenced corrosion was investigated in the early failed copper pipes by pitting used in underground water.The bacteria were cultured by sampling from corrosion product near pit
In this work,the passivation behavior and galvanic corrosion of 304 stainless steel elbow under erosion-corrosion(E-C)condition were studied by array electrodes technique through a loop system.
The corrosion behavior and mechanism of under deposit corrosion of ammonium chloride salt of 10# carbon steel under various temperatures and relative humidity were investigated by the weight loss meth
With wide application of electronic products,they are becoming an indispensable part of our life.The service life of electronic components is attracting more and more attention.