5. Ho3+/Er3+ co-doped fluoride glass sensitized by Tm3+ pumped by a 1550 nm laser diode for efficient 2

Ho3+/Er3+ co-doped fluoride glass sensitized by Tm3+ pumped by a 1550 nm laser diode for efficient 2

来源 :The 24th International Conference on Glass( ICG Congress 201 | 被引量 : 0次 | 上传用户：baalzio

【摘 要】

：

In present paper, a high emission intensity of 2.0 μm is reported of Er3+/Ho3+ co-doped fluoride glass sensitized by Tm3+ ions under 1550 nm excitation.

【作 者】

：

Feifei Huang Ying Tian Huanhuan Li Shiqing Xu Junjie Zhang 

【机 构】

：

College of Materials Science and Engineering, China Jiliang University, Hangzhou, 310018, China

【出 处】

：

The 24th International Conference on Glass( ICG Congress 201

【发表日期】

：

2016年11期

下载到本地 , 更方便阅读

下载此文 赞助VIP

声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架

论文部分内容阅读

In present paper, a high emission intensity of 2.0 μm is reported of Er3+/Ho3+ co-doped fluoride glass sensitized by Tm3+ ions under 1550 nm excitation.

其他文献

非均匀张力作用下运动薄膜的稳定性研究

轴向运动连续体系统中，其动力学特性呈现为横向振动和不稳定性，横向振动使系统产生不稳定性，限制了它们的应用效果。轴向运动系统的控制方程中含有时间和空间混合偏导数项，是典型的陀螺连续体，运动微分方程中包含着丰富的动力学内容。由于技术流程的要求，在高速运动印刷包装系统中，出现张力的不均匀性是显而易见的，因此必须考虑在非均匀张力作用下，系统会产生的动力学行为。图1 所示，在非均匀张力作用下以恒定速度轴向运

会议

Fracture problem of a nonhomogeneity high temperature superconductor strip based on real fundamental

To analyze the fracture problem of the nonhomogeneity high temperature superconductor(HTS)strip under electromagnetic force,we derive the real fundamental solutions based on eigenvalue and eigenvector

会议

nonhomogeneity high temperature superconductorreal fundamental solutionssingul

Nano-structured glass ceramics for color tunable white LED color converter

Inorganic color converters such as phosphor ceramic (PC) and phosphor-in-glass (PiG) have been now commercialized to replace organic resin which suffered from weak thermal and chemical stabilities for

会议

2.7μm emission in oxy-fluoride glass ceramics containingLuOF∶ Er3+ nanocrystals

Er3+ doped transparent oxy-fluoride glass ceramics containing LuOF nanocrystals was prepared by traditional melt-quenching and subsequent thermal treatment method.The influence of thermal treatment te

会议

Oxy-fluoride glass ceramicsLuOF nanocrystals2.7 μm luminescence

Cordierite based nano microcrystalline glass

In order to get Nano-sized cordierite glass-ceramics, different kind of nucleation catalysts was tested in the cordierite base glass , such as TiO2, Zr2O3, and admixed TiO2-Zr2O3.

会议

cordieritenucleation catalystsheat treatmentnano microcrystalline glass

Vanadium phosphorus sealing glass crystallization stability of antimony-doped

80V2O5-20P2O5-xSb2O3 (VPS) (x =1, 3, 5 mol%) Glasses were prepared.The crystallization stability analysis of VPS glass were investigated.The effect of Sb2O3 on crystallization lower limit temperature

会议

Sb2O3vanadium phosphate glass51V Static NMRcrystallization stability

Phase separation and crystallization processes during nuclear glass synthesis

Nuclear waste glasses are produced by a succession of physical and chemical interactions between a solid waste (calcine) and a glassy precursor (glass frit) through a high-temperature vitrification st

会议

Phase separation in the Na2O-B2O3-SiO2-Fe2O3 glass-forming system

Adding Fe2O3 to sodium borosilicate (SBS) glass-forming system gives such glasses a number of valuable properties, which makes it possible to use them for producing semiconducting fibers, glass enamel

会议

Phase separation and the effect of B2O3 and P2O5 addition in RO-Al2O3-SiO2 system

The phase separation of glasses of the 17(CaO+MgO)-6Na2O-6AhO3-65SiO2-x(B2O3 +P2O5)(0 ≤ x ≤6) (wt%) series were investigated using DSC, XRD and SEM.The X-ray diffraction (XRD) and differential scannin

会议

Towards macroporous silica monoliths by phase separation and leaching of chemically modified sodium

Porous glasses are the products of phase separation and chemical leaching of glasses with a certain composition.Phase separation occurs, if glasses, whose compositions are within a "mixing gap" of a c

会议