【摘 要】
:
Three kinds of Nb-Ti-Mo ferrite matrix micro-alloyed steels with three different Ti contents were designed.With optical microcopy,transmission electron microcopy,energy spectrum analysis and tensile t
【机 构】
:
National Engineering Research Center for Advanced Rolling Technology,University of Technology Beijin
论文部分内容阅读
Three kinds of Nb-Ti-Mo ferrite matrix micro-alloyed steels with three different Ti contents were designed.With optical microcopy,transmission electron microcopy,energy spectrum analysis and tensile test,the microstructures,precipitate particles as well as mechanical properties of three steels were studied.The strength and toughness of steel with0.092%Ti content were verified to adequate for Q600 grade refuge alternative plates.The results show that there were two kinds of particles with obvious different size in ferrite micro-alloy steels.The dominating precipitates are compound carbonitrides of Nb,Ti and Mo,which are less than 10nm and precipitated in chains or dispersed in the interior of grain.Another kind of particles are titanium carbonitrides with size about 200-300 nm.By the method of tensile tests at room temperature and at 500°C,the Nb-Ti-Mo ferrite matrix micro-alloyed steels have excellent mechanical properties.In addition,the samples with 0.092%Ti content have yield strength at 500°C exceeding400MPa,which are suitable as refuge alternation-plates.
其他文献
Hydrocarbon pipelines transporting compressible products like methane or high-vapor-pressure(HVP)liquids under supercritical conditions can be susceptible to long-propagating failures.As the unplanned
With the increase of wall thickness of pipeline steel,DWTT fracture toughness has become more and more sensitive to production process,including alloy design and processing,so it need more tight and m
Repeated deformation with optimum reductions in roughing mill exceeds the critical amount of strain required for recrystallization to occur.Recrystallization during roughing mill rolling refines auste
Over the past twenty years,significant advances have been made in the field of microalloying and associated application,among which one of the most successful application cases is HTP practice for hea
The susceptibility to hydrogen embrittlement in high strength mooring chain steel with different boron content(0,0.003%,0.008%)were investigated by electrochemical hydrogen charging technique and tens
This paper analyzes precipitation and dislocation strengthening behaviors of a 27mm thick Niobium-bearing Grade X80 steel plate for strain based design line pipe manufacture.The steel is produced by t
Extensive investigations of metallurgical roles played by Nb microalloying in advanced products of seamless steel tube have been carried out.The results show that with Nb microalloyed,the recrystalliz
With the exploitation of gas mixed with sulfur,the requirement of hydrogen induced cracking(HIC)resistance for medium carbon vessels serving at environmental with hydrogen sulfide solution become more
The effect of austenite deformation and continuous cooling on the evolution of microstructure in a high temperature processing(HTP)concept pipeline steel was investigated in this research.It was found
This study is focused on the effect of vanadium addition to an API X100 steel.Laboratory heats were melted and control rolled based on a coil plate production process.Compared to non vanadium steel,it