Toward the Quantification of the Cement Paste Content of Fine Recycled Concrete Aggregates by Salicy

来源 :The 14th International Congress on the Chemistry of Cement ( | 被引量 : 0次 | 上传用户:ialyialyialy
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
  Recycled concrete aggregates (RCA) are mainly composed of an intimate mix between natural aggregates and cement paste and the complete separation between these two phases is difficult.Cement paste generally presents a much larger porosity than natural aggregates, the content and the physicochemical properties of cement paste therefore have a large influence on the properties of RCA.Any method seems to be adapted to the characterization of cement paste content (CPC) in fine recycled concrete aggregates (FRCA) especially for RCA containing calcareous aggregates.
其他文献
In order to evaluate resistance of salt scaling of concrete, the new evaluation test method with small amount of sample for short period was investigated in this study.Test method proposed was as foll
Cement pastes incorporated with 0%, 15%, 25% and 35% of fly ash by weight were prepared.Alter 90d ot curing, the cement pastes were crushed and ground into powders with a particle size less than 0.080
In this paper, the accelerated method was conducted to investigate the ASR reactivity of two cherts (Yoro and Seto) which were used as aggregate materials for concrete mixing.The reaction was stopped
The formation and transformation characteristics of ettringite played an extremely important effect on the accelerated hardening and expabsion of concrete as well as its long term durability.The stabi
The alkali-silica reaction (ASR), leading to serious structural degradation, is the chemical reaction between reactive silica presenting in aggregates and hydroxyl ions from cement paste or pore solut
会议
The need to limit the environmental impact of cementitious materials and to dispose of by-products such as fly ash and slag leads to the increasing use of supplementary cementitious materials (SCMs).I
Water confined within the nano-to microscale pores of cementitious materials plays a crucial role in damage processes affecting the sustainability of cement pastes, especially for the binding material
Over the last two decades, there has been an increased focus on the stability of the cement sheath under the influence of shear stresses imposed during the lifetime of the well.Shear stresses can occu
The influence of a new type of antifreeze-reinforced material (AFRM) on Vc value, strength, freeze-thaw resistance, water absorptivity and void parameters of roller compacted concrete (RCC) were inves
Owing to environmental and commercial pressures the constitution of Portland cement formulations is changing towards having higher aluminosilicate contents.Mainly these changes are achieved by adding