【摘 要】
:
The conditions to control the fatigue crack of steel bridges are the geometric state,the initial characteristic construction state,materials,and the load conditions.Among them,the greatest effect on f
【机 构】
:
Department of Inspection Division,KISTEC,Goyang-City,Korea
【出 处】
:
The 7th International Conference on Bridge Maintenance, Safe
论文部分内容阅读
The conditions to control the fatigue crack of steel bridges are the geometric state,the initial characteristic construction state,materials,and the load conditions.Among them,the greatest effect on fatigue crack is the stress history that was measured by using a strain gauge in the field.Therefore,in order to study the fatigue safety of bridges and the causes of the fatigue cracks more accurately,fluctuating stress measurement is required for proper data acquisition.(Jang et al 2000)
其他文献
The seismic-resistant design of structures,is generally performed under a unique ground motion excitation at the base,regardless its type,shape and planar extension.However,for extended structures,suc
Deterioration of steel cable-stayed bridges is often found in stay cables,steel girders and foundations.Structural durability problems mainly contain fatigue and erosion of the cables and steel girder
Structural characteristics are extremely important to the durability design process of concrete bridge,yet are not considered sufficiently by the design parameters in current durability design codes a
Steel orthotropic bridge deck is the only system likely to provide a service life exceeding 100 years with minimum maintenance; however,concerns of inservice fatigue cracking from welded connections,a
The traffic load effects on existing bridges may be quite different from those of design live loads due to various traffic environments.However,the bridge maintenance and safety assessment of in-servi
Some high-temperature environment would cause a comparatively large loss ofpre-stress on pre-stressed CFRP plate or give rise to failure due to the unstable holding of anchor holder on CFRP plate,when
A large number of long-span bridges in mainland China have been constructed,which become the motivation of applications of structural health monitoring (SHM) technology.Many bridges have been implemen
Due to their various advantages including excellent corrosion resistance and high strength-to-weight ratios,fibre-reinforced polymer (FRP) composites have been widely used as strengthening materials t
The increasing stock of short and medium span bridges in this region and around the world induces substantial maintenance and rehabilitation costs which result in a significant increase in financial b
Complex bridges are owned and maintained by many agencies worldwide.Most complex bridges consist of hundreds or thousands of elements,and each element typically requires careful,individual condition a