通过熔融共混法制备聚乳酸(PLA)/聚对苯二甲酸-己二酸-l,4-丁二醇共聚酯(PBAT)/有机蒙脱土(OMMT)三元共混物,研究了不同加工条件下,蒙脱土纳米粒子对共混物微观形貌的影响,并结合纳米粒子选择性分布效应对其增容机理进行了初步探时。
蒙脱土对PLA/PBAT共混体系微观形貌的影响
【摘 要】
：
通过熔融共混法制备聚乳酸(PLA)/聚对苯二甲酸-己二酸-l,4-丁二醇共聚酯(PBAT)/有机蒙脱土(OMMT)三元共混物,研究了不同加工条件下,蒙脱土纳米粒子对共混物微观形貌的影响,并结合纳米粒子选择性分布效应对其增容机理进行了初步探时。
【机 构】
：
海南大学材料与化工学院,海南海口570228
【出 处】
：
The 11th China-Japan joint conference on Composite Materials
【发表日期】
：
2014年3期
其他文献
为提高针叶树材木质素基碳纤维的力学性能,通过熔融纺丝法制备的聚乙二醇木质素纤维先经过85℃的lHC1与C6H12N4混合水溶液化学固化lh,再在空气氛围中以一定的升温速率从室温加热至250℃氧化热稳定处理,制备得到无表面缺陷的不熔融纤维和经碳化后的碳纤维.研究表明,在化学固化过程中,由ChH12N4分解得到的甲醛分子在木质素分子中的苯环之间形成亚甲基键连接,提高了水质索分子的交联程度,并且在纤维表
Activated carbon fibers (ACF) were prepared from liquefied wood through liquefaction,melt-spinning,curing,carbonization,and stream activation.Their microstructure including crystal structure,surface m
Surface Modification of Bamboo Fibers and Its Effect on Reinforcing Unsaturated Polyester Composites
Bamboo fiber reinforced unsaturated polyester (UPE) composites were prepared by compression molding.Effects of morphology and chemical modification of fibers on the mechanical properties and water abs
会议
本论文对术材液化物水洗不溶微球进行了研究，利用不同洗涤工艺可制备木材液化物微球，并对其微观结构、热性能、化学结构进行了探讨和分析。结果表明，水浴温度70℃的中性水水洗工艺制备的杉木、杨木液化物微球在数量、球形度、表面致密性等方面均优于常温水水洗工艺和盐酸水溶液洗涤工艺，前者的灰份含量则低于后两者。
Preparation of Rice Straw Power by Mechanical Grinding Process and the Mechanical Properties of Thei
Different methods were used to grind rice straw (RS) to obtain the rice straw powders.The biodegradable composites were prepared with the RS and poly (lactic acid)(PLA).Mechanical properties of the bi
The purpose of this study is to investigate the mechanical properties of binder-less composites made from lignin and cellulose extracted from bamboo.The bamboo biomass was decomposed by the superheate
Aluminum-polyphenylene sulfide single lap joints were prepared by aluminum pitting corrosion.The joint strength was estimated in relation to structural information measured using scanning electron mic
In this study,effect of hot water treated rice straw on the mechanical properties of rice straw/poly (lactic acid) (PLA) composite was investigated.The optimal treated condition was observed by changi
One of the most important issues for the design of filament-wound pressure vessels reflects on the determination of the most efficient meridian profiles and related iber architectures.
本文使用硅烷偶联剂KH550对介孔分子筛MCM-41进行表面修饰后添加到环氧树脂中，制备得到环氧树脂/MCM-41复合材料。采用热分析、扫描电镜、傅里叶红外光谱、X衍射、氮气吸附-脱附等手段对表面修饰前后的MCM-41进行结构表征，并对复合材料的力学、热学和电气性能进行测试。本文利用差示量热扫描仪熏点研究了环氧树脂/MCM-41复合材料的固化动力学，通过n级模型得到复合材料固化过程的反应级数、活化
会议