The corrosion performance of high strength weathering steel with Cu,Cr micro-alloying under as-rolled,annealed,normalized,and TMCP states was studied.Result
【机 构】
:
College of Materials Science and Engineering,Nanjing University of Aeronautics and Astronautics,Nanj
论文部分内容阅读
The corrosion performance of high strength weathering steel with Cu,Cr micro-alloying under as-rolled,annealed,normalized,and TMCP states was studied.Results showed that the microstructures of steels under as-rolled,annealed and normalized states were composed of pearlite and ferrite.Average grain size of as-rolled steel was the largest,followed by annealed and normalized.The microstructure of TMCP was mainly consisted of martensite.The corrosion potentials of naked steels in TMCP,as-rolled,annealed and normalized states had little difference,but the corresponding corrosion currents were 0.1287× 10-5A·cm-2,0.4418 × 10-5A·cm-2,0.7364× 10-5A·cm-2 and 1.064× 10-5A·cm-2,respectively.However,the variation tendency of polarization resistance was contrary to the corrosion currents.After two months,the polarization resistance of the TMCP steel decreased to 1304 ·cm2,but the annealed,as-rolled and normalized steel increased to 1881Ω·cm2,1561Ω·cm2 and 1068Ω·cm2,respectively.The arrangement of annual corrosion rate from high to low was: normalized,as-rolled,annealed and TMCP steel,and the rule of rust layer from thick to thin was similar.
其他文献
Thermal simulator and transmission electron microscope(TEM)were adopted to investigate the precipitation behavior in different stage of controlled rolling,c
The E690 grade offshore platform steel was obtained by top and bottom blowing converter,curved spray continuous casting machine and thermo-mechanical contro
As a kind of impurity and displaying with FeS and MnS form in steel,Sulfur can make the disadvantage effect on the performance of hot-working,welding and co
为了了解五大连池火山熔岩地貌土壤主要矿质养分含量及其特点,同时探讨苔藓植物对土壤养分积累的影响,选取了形成年代不同的六座火山,对其进行了苔藓植物生境分布、盖度调查
Microstructure evolution and impact thoughness of V-N-Ti and Nb-V-Ti microalloyed bulb flat steel in rolling process have been investigated.The results indi
Improving the material of axles is not only used to enhance the reliability of the use of railway wagon axle,but also an effective means to raise railway tr
The results of experiments show that Nb can significantly lower phase transformation temperature and refined both lamellar space of pearlite and pearlite co
Hot compression tests were performed on gleeble-3800 thermal simulation machine to study the effect of different deformation parameters on microstructure of
The demand for more sustainable development promotes the need for components and steel structures with a longer useful life and better performance.Upgrade o