【摘 要】
：
The efficient conversion of glucose to produce 5-hydroxymethylfurfural (5-HMF) and levulinic acid (LA) were investigated in aqueous media promoted over Lewis acid InCl3.The optimization of reaction co
【机 构】
：
Beijing Key Laboratory of Lignocellulosic Chemistry,College of Materials Science and Technology,Beij
论文部分内容阅读
The efficient conversion of glucose to produce 5-hydroxymethylfurfural (5-HMF) and levulinic acid (LA) were investigated in aqueous media promoted over Lewis acid InCl3.The optimization of reaction conditions were manipulated through reaction temperature,time.The yield of 5-HMF derived from glucose was obtained with 80% in 20 min at 180 oC.The highest yield of LA obtained from 5-HMF hydrolysis was 57% using 3 wt % InCl3.Furthermore,a plausible reaction mechanism for the dehydration of glucose was proposed based on the results.The results show that InCl3 as an active Lewis acid catalyst demonstrated excellent activity in glucose isomerization to fructose and dehydration/rehydration reactions.
其他文献
为了防治大气污染、水质污染和恶臭等公害,活性炭在环境保护方面也得到了越来越广泛的应用.柠条作为沙生灌木中的一种,在内蒙古地区具有丰富的资源,采用柠条制备活性炭,可以开拓沙生灌木资源的利用途径,对内蒙古地区的经济建设和生态建设具有重要的意义.本文采用活化法制备柠条活性炭,选用氯化锌和磷酸两种活化剂,以亚甲基蓝吸附量为评价指标,用正交试验法确定了浸渍比、活化剂浓度、活化温度、活化时间四个影响因素下的较
本文采用木质纤维素和蒙脱土插层复合制备出的纳米复合材料作为吸附剂,进行了模拟含铅废水中Pb2+的吸附实验研究,考察了含Pb2+溶液的初始浓度、pH值、吸附温度和吸附时间对溶液中Pb2+去除效果的影响.结果显示,最佳吸附条件是在Pb2+溶液初始浓度0.04M、pH值6.0、吸附温度30oC、吸附时间60min时,平衡吸附容量达到最大值140.9mg/g.测定了吸附动力学曲线和吸附等温线,结果表明,吸
综合考虑了豆粕溶液的固含量、粘度,底物浓度的影响,选取浓度为20％的豆粕溶液作为研究对象,对豆粕溶液在胃蛋白酶作用下的水解特性进行了深入研究.考查了豆粕中的蛋白质的水解度随酶解温度、酶解时间、pH值,酶添加量的变化规律,以及酶解前热处理对酶解效果的影响.结果表明:酶解前热处理能改善酶解的效果,有利于水解反应的进行,提高水解度.豆粕溶液在90℃下预热处理10min后,在水解工艺为温度37℃、pH1.
本文简要回顾了机械浆发展历程.漂白技术的发展推动了机械制浆技术的进步.在节约资源与保护环境的压力下,90％的高得率、90％ISO的高白度和90N.m/g的高抗张强度的"三高"制浆技术将成为造纸工业制浆技术的努力方向.近三十年以来,先后出现了APMP和P-RC APMP制浆技术,机械浆漂白方面值得关注的新型漂白技术是:磨浆机漂白技术;连二亚硫酸钠强化螯合的漂白技术,以Mg(OH)2或MgO为碱源的过
A novel type of hierarchically biomorphic carbons (HBCs) with macro-/ microporous and ordered mesostructure has been successfully prepared by using wood as a mimetic template to reproduce the wood cel
本文主要针对强化改性杨木(利用可聚合的不饱和乙烯类单体浸渍杨木,然后通过引发剂将单体聚合成高分子聚合物,通过加热聚合而成的改性材),采用现代先进的分析测试技术傅立叶红外光谱(FTIR)和扫描电镜,定性分析了强化改性杨木的化学组成以及各基团的变化,从微观角度解释了强化改性杨木表面结构分析.
采用微波法制备了松香树脂酸烯丙酯,并利用单因素和正交试验法对其工艺条件进行了优化,单因素实验表明,随着微波功率的增大、反应时间的延长、反应温度的增加、氯丙烯与树脂酸钠物质的量比值的升高及催化剂用量的增加,树脂酸烯丙酯的收率先升高后降低.正交试验结果表明,影响产物收率的主要因素是微波功率,所考察5个因素的影响强弱顺序为微波功率＞反应时间＞物料配比＞催化剂用量＞反应温度,最佳反应组合为A3B4C4D4
本文主要针对杨木单板强化改性材(利用可聚合的不饱和乙烯类单体浸渍杨木单板,然后通过引发剂将单体聚合成高分子聚合物,通过加热聚合而成的改性材),采用现代先进的分析测试技术傅立叶红外光谱(FTIR)和扫描电镜,定性分析了杨木单板强化改性材的化学组成以及各基团的变化,从微观角度解释了杨木单板强化改性材表面结构分析.