In recent years a great zeal for natural textile fibres has increased throughout the world.Bamboo fibre being natural has recently attracted environment concerned researchers.The chemical composition
【机 构】
:
Department of Applied Chemical Sciences & Technology, Guru Nanak Dev University, Amritsar, India
【出 处】
:
The 12th Asian Textile Conference (第12届亚洲纺织会议暨2013年纺织学术年会)
论文部分内容阅读
In recent years a great zeal for natural textile fibres has increased throughout the world.Bamboo fibre being natural has recently attracted environment concerned researchers.The chemical composition of bamboo is similar to other bast materials.
其他文献
Toughness is a critical issue that limits hydrogel application.Generally speaking, polymer hydrogels are soft and brittle.They cannot withstand large deformations.
Cotton fabric is popular natural raw material which is commonly used in fabric.Cotton fiber has good moisture absorption capacity;the fiber is soft and surface is smooth, Cotton has excellent wearing
UHMWPE (ultra-high-molecular-weight polyethylene) fiber has the highest specific modulus and strength of all commercial reinforcing fibers due to its excellent tensile modulus and low density.
In this study, the Polylactic acid (PLA)-based membrane was manufactured by the technique of electronspinning.The specific characteristics of the nano-fibrous membrane, which is ultra-high BET surface
In recent years, nanofibers are recognized as an exciting new class of material for various applications.One of the well-known methods for the production of nanofibers is electrospinning, however it c
The hydrolysis of cyano and ester groups from polyacrylonitrile fiber and pulp was accelerated by cationic surfactant in alkaline aqueous solution.
Polytetrafluoroethylene (PTFE) fiber was prepared through a series of processes including paste extrusion facilitated by lubricant, rolling of the extrudate into belt, high temperature stretching, and
Renewably sourced polymer is also called bio-based polymer, which is derived from renewable biomass sources, such as vegetable fats and oils.
A p-aramid fiber has great fibril structure which are easily split resulting in nanofiber.Due to the strong hydrogen bonds among p-aramid molecules, split nanofiber structures three-dimensional networ
The cellulose is modified for high yield of hydrolysis.A new 1,3,5-triazine derivative 2-(4-aminobenzenesulfonate sodium)-4,6-dichloro-l,3,5-triazine (ASACT) was synthesized from 2,4,6-trichloro-l,3,5