Solution-Temperature-Controlled Growth of Microarc Oxidation Coatings on Aluminum Substrates

来源 :2014中国功能材料科技与产业高层论坛 | 被引量 : 0次 | 上传用户:mechanical123
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
  The growth of microarc oxidation (MAO)coatings on aluminum substrates was controlled via changing solution temperature from 10 to 60 ℃.The results show that an elevation of the temperature lowers the applied voltage and the coating thickness.
其他文献
本文首先分析了某电厂0Cr18Ni9不锈钢冷却水管发生穿孔的形貌和产生孔蚀的原因,并指出了在这种运行条件下防止孔蚀的措施。研究结果表明:0Cr18Ni9不锈钢冷却水管产生孔蚀的原因是水质中含有较多的Cl-和容易结垢的Ca2+、Mg2+,腐蚀的产物主要为Fe和Cr的氧化物;防止产生孔蚀的经济措施是提高水质的pH,并降低水质中的Ca2+、Mg2+含量。
Solar grade silicon and modified Al-Si alloys are widely used in the world.These two favored materials are expected to obtain by the electromagnetic directional solidification of hypereutectic Al-Si m
在碱性条件下,以溴代异丁烷为卤化剂对壳聚糖进行化学改性,得到异丁基壳聚糖,异丁基壳聚糖与氯化钙溶液在pH 6.0的条件下充分反应得到异丁基壳聚糖钙的复合物,用红外光谱及紫外光谱对产物的结构进行表征,并测定了产物中的钙含量.
以廉价的Sb2O3为锑源经两步反应制备了BaSb2O6光催化剂,探索了反应条件(温度、时间)对光催化效率的影响,以亚甲基蓝染料溶液的脱色降解实验为模型反应考察了样品的光催化性能,结果表明,在500w紫外灯照射40min,亚甲基蓝的脱色率达到90%以上。
Process optimization of the synthesis of vanadium nitride from vanadium pentoxide and carbon black using microwave carbothermal nitridation method at atmospheric pressure was performed using response
In this paper, tensile properties at room temperature and bending rupture properties of single crystal aluminum wire, 4mm in diameter, fabricated by ohno continuous casting were studied, and its fract
以有机碱二乙烯三胺(EDTA)为碱源,Sm(NO3)3·6H2O为钐源,在不同模板剂辅助条件下采用水热-热处理相结合的方法进行Sm2O3纳米晶的可控合成。利用X-射线衍射仪(XRD)、扫描电子显微镜(SEM)和Lambda 950分光光度计分别对产物的物相、形貌和光学性能进行表征,并研究了未添加模板剂和分别以六亚甲基四胺(HMTA)、聚乙烯吡咯烷酮(PVP)和十六烷基三甲基溴化铵(CTAB)为模板
Epoxy protective coatings incorporated with polyaniline nanowires were prepared and characterized.Diglycidyl ether of bisphenol A was used as matrix epoxy and phenalkamine synthesized from cardanol wa
本文采用水热法制得了具有较高光催化活性的4ZnO·B2O3·H2O,并采用XRD、SEM对产物的晶相组成和显微型貌进行了表征,研究了不同前驱液pH值条件下的制得的4ZnO· B2O3·H2O晶体在紫外光下分别对三种有机染料(亚甲基蓝、罗丹明B和甲基橙)的光催化性能,并首次测试了所制4ZnO·B2O3· H2O晶体的禁带宽度。
以SnCl4·5H2O和NH3· H2O为主要原料,水为反应介质,在微波水热条件下研究了不同反应温度对SnO2的结构和光催化性能的影响。利用X射线粉末衍射仪(XRD)、扫描电子显微镜(SEM)、透射电子显微镜(TEM)和光催化反应仪等对产物进行表征测试。