【摘 要】
:
Among the various hydrogen storage materials,theMgH2-2LiNH2systemis regarded as a promising candidate for on-board application due tothe moderate operation temperature,good reversibility,and a relativ
【机 构】
:
General Research Institute for Nonferrous Metals,Beijing,100088,China
【出 处】
:
第十五届全国氢能会议暨第7届两岸三地氢能研讨会
论文部分内容阅读
Among the various hydrogen storage materials,theMgH2-2LiNH2systemis regarded as a promising candidate for on-board application due tothe moderate operation temperature,good reversibility,and a relatively high capacity of 5.6 wt. %.The theoretical dehydrogenation temperature of the MgH2-2LiNH2 systemis about 90 ℃ under 0.1 MPaequilibrium hydrogen pressure [1].
其他文献
我国超硬材料发展,有独自的特点,超高压高温装备和工艺制定。国外比如美国、瑞典、爱尔兰和芬兰,它们合成金刚石和金刚石二次聚合的聚晶(当然包括立方氮化硼)都是在两面顶压机上完成的。我国采用的都是铰式六面顶压机。尽管在可操作性上增加一些可变因素,但它是可以克服的。实践证明就是如此。铰式六面顶压机最大特点是便于大型化,易于提高吨位、增大金刚石合成腔体,为优质增产提供了有力保证。从金刚石研制成功(包括立方氮
利用储氢密度大于1.8wt%、易活化(活化温度<90℃)、吸放氢平台性能较好且具有实用价值的TiFe0.94Mn0.04储氢合金,设计了3种不同结构的储氢装置,重点研究了TiFe0.94Mn0.04合金吸放氢过程中储氢装置表面应力、应变规律,从而为TiFe系储氢装置的抗膨胀结构设计提供参考依据.
开发高容量的储氢材料是目前储氢领域研究的重点.LiNH2BH3的储氢容量为13.7wt %,因此吸引了很多研究者的关注[1,2].按照反应示意图1所示,利用通过静电纺丝法得到的含有Li3N纳米颗粒的介孔作为纳米反应器[3],在氩气气氛中与NH3BH3(AB)的四氢呋喃溶液进行反应制备包覆在纳米碳纳米纤维中的高分散性的LiNH2BH3(LiAB)纳米颗粒(LiAB@CNFs).
The catalytic effects of transition metal carbides TiC,ZrC,Cr3C2 and WC on the dehydrogenation properties of LiAlH4 prepared by high energy ball-milling are investigated in this paper.Hydrogen storage
Microstructures and electrochemical characteristics of LaNi3.55Co0.2-xMn0.25Al0.15Cu0.75(W0.7Fe0.3)x(x=0-0.20) hydrogen storage alloys are systematically investigated.X-ray diffraction and backscatter
In this work,a thin double-layered annulus metal hydride bed was fabricated for fast transfer of the mass and heat during the hydrogen recovery and delivery processes.The properties of hydrogen recove
金属有机骨架化合物(MOFs)具有高比表面积且结构易于修饰等优点,在储氢领域显示出良好的应用前景[1].但是,MOFs在温和条件下(近常温常压)的储氢容量仍然低于实际应用的要求.研究表明在MOFs中引入某些贵金属纳米粒子可以通过增强氢气分子与MOFs的相互作用从而提高室温储氢容量[2-4].
本文通过高能球磨MgH2和α-Fe的混合物,制备出一种MgH2-Fe的纳米复合材料,并对该材料的物相组成、微观结构及其储氢性能进行深入研究.PCT(pressure-composition-temperature)测试结果表明,MgH2-Fe中的Mg的氢化焓为-66.8kJ/mol H2,相对于纯MgH2中的Mg的氢化焓有所降低,而Mg的吸放氢过程的滞后现象也得到抑制.与此同时,这种纳米复合材料的
In recent years,some of the new series of RE-Mg-Ni-based AB3 and A2B7-type alloys were considered to be the most promising candidates for high energy and high power Ni/MH batteries owing to their high
Mg-based hydrogen storage materials have received considerable interests due to their low cost,great abundance,and high hydrogen storage capacity (7.6 wt %for MgH2,3.6 wt %for Mg2NiH4) [1,2].However,t