染料排放会对水体环境造成严重污染。本课题结合Fe3O4的磁性和Nb2O5对染料的强降解以及良好的循环使用效果，构思合成 Fe3O4/Nb2O5新的复合材料，以及探究其对于染料废水的降解和循环使用效果。
Fe3O4/Nb2O5复合材料光降解性能研究
【摘 要】
：
染料排放会对水体环境造成严重污染。本课题结合Fe3O4的磁性和Nb2O5对染料的强降解以及良好的循环使用效果，构思合成 Fe3O4/Nb2O5新的复合材料，以及探究其对于染料废水的降解和循环使用效果。
【机 构】
：
郑州轻工业学院,材料与化学工程学院,郑州,450002
【出 处】
：
河南省化学会2016年学术年会
【发表日期】
：
2016年10期
其他文献
Photocatalytic and membrane separation coupling technology will photocatalytic technology coupled with membrane separation technology,realized the two technologies in the same processing unit founctio
本文以乙二醇和乙醇为溶剂，柠檬酸钠为络合剂，采用溶剂热法用乙二醇同时还原氧化石墨和氯化钯制备了 Pd/石墨烯催化剂，研究了柠檬酸钠加入量对催化剂结构和催化甲酸氧化性能的影响。采用透射电镜(TEM)、X射线衍射(XRD)、循环伏安和计时电流对催化剂进行了表征和性能评价。
ZnSnO3 visible-light-responsive photocatalyst was synthesized through template route by the way of plant mediation,then to evaluate the photocatalytic activities of the synthesized materials according
Extractive Separation of 4-Hydroxylpyridine with Co-extractant of Di(2-ethylhexyl)Phosphoric Acid an
In our previous work,reactive extraction using di(2-ethylhexyl)phosphate acid(D2EHPA)has been successfully used for the separation of 4-Hydroxylpyridine(4HP)from the aqueous solution.
本文通过原子力显微镜研究了两步阳极氧化的方法制备阳极氧化铝(AAO)膜的各影响因素。结果表明,AAO 膜为垂直于氧化铝膜表面平行生长的结构,呈类蜂窝状的六边形,孔洞孔径尺寸的范围为40～100 nm,分布均匀。
会议
Effects of cationic cetyltrimethylammonium bromide on aggregation behaviors of sodium lignosulfonate
Effects of cationic cetyltrimethylammonium bromide(CTAB)on aggregation behaviors of sodium lignosulfonate(NaLS)in concentrated solutions were investigated by rheology,conductivity,zeta potential and s
Due to traditional fossil fuel consumption and consumption demand increasing,meanwhile,increasing greenhouse emission results in global climate change,in the next few years,the use of non-renewable re
Facile synthesis of one-dimensional hierarchical LiNi0.8Co0.15Al0.05O2 microrods:towards better rate
One-dimensional hierarchical LiNi0.8Co0.15Al0.05O2 microrods are synthesized through lithiation of mixed Ni,Co and Al oxalate microrods obtained via a two-step co-precipitation route.
SnO2 is a conventional n-type metal oxide gas sensing material with terrible selectivity,stability and high intrinsic resistance.