Effects of Duration on Wear Rate of A PTFE Composite

来源 :2014中国功能材料科技与产业高层论坛 | 被引量 : 0次 | 上传用户:jzlh6890
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
  A type of PTFE/MoS2/glass fiber composite has been used as bearing cage material.To study the friction properties, the tests have been performed under various parameters on block-on-ring.The experimental results were as follows: Wear rate of the polymer composites was dramatically affected by test duration.
其他文献
A new and facile method for improving the procedure of anodic aluminum oxide (AAO) film preparation was presented, which was based on an electrochemical detachment procedure.
By controlling the cooling, mean temperature adjustment and isothermal cooling process, bainite and martensite can be produced in the surface and the core of the ductile iron gear using the 75℃ hot wa
A series of ZnO (TiO2)/CdTe, CdSe, CdS single shell and CdSe/CdTe double shell nanocable arrays were prepared as the photoanodes for quantum dots sensitized solar cells (QDSSCs).
会议
Anoxide-alumina-silicacoating which would to improve the oxidation resistance of carbon fibers was prepared by sol-gel method.XRD and SEM were used to characterize the surface appearance and phase tra
The films of polypropylene/modified carbon fibers (PP/MCF) were made by physical blending method under refluxing and stirring for 3h at 130 oC.
海水环境下服役的混凝土会经历一系列物理和化学侵蚀过程。通过先进测试技术,表征了海水和淡水环境下混凝土孔结构和界面过渡区,采用压汞法和扫描电镜等先进技术探索了海水环境下混凝土孔结构和界面过渡区的演变规律以及矿物掺合料对混凝土孔结构和界面过渡区的改善作用。
The piezoresistivity of activated nano-carbon reinforced cement-matrix composites (CBPCs) with different styrene-butadiene rubber (SBR) content are experimentally studied.An interesting phenomenon of
会议
Porous poly(1-naphthylamine) were synthesized by interfacial polymerization method.The effects of several reaction conditions including oxidant/monomer molar ratio, polymerization temperature and reac
In order toincrease the electrical conductivity greatly but maintain a large Seebeck coefficient and a low thermal conductivity simultaneously, the binaryphased LaCeFe3CoSb12-Sb nanocomposites compose
目前使用的氮化物LED一般生长在蓝宝石衬底上.该技术存在几个严峻的问题:一方面,蓝宝石价格昂贵,使得氮化物器件生产成本高昂;另一方面,蓝宝石热导率低,不利于开发高功率氮化物器件;再次,基于蓝宝石上的LED核心技术几乎已全部欧美国家垄断并申请了专利.
会议