【摘 要】
：
This paper studies the synthesis ofbio-nano-SiO2 on rice straw surface and APP by in situ polymerization, which rice straw was considered as the dispersed phase, ammonium polyphosphate (APP) was consi
【机 构】
：
College of Materials Science and Engineering,Nanjing Forestry University,Nanjing 210037,China
【出 处】
：
第二届中国国际复合材料科技大会 (CCCM-2)
论文部分内容阅读
This paper studies the synthesis ofbio-nano-SiO2 on rice straw surface and APP by in situ polymerization, which rice straw was considered as the dispersed phase, ammonium polyphosphate (APP) was considered as the reactive monomer.The mechanism of in situ polymerization between bio-nano-SiO2 and APP was characterized by FTIR, SEM, TG.
其他文献
Palygorskite/carbon composites were synthesized via a hydrothermal route at 220℃ for 24h using palygorskite and cellulose as raw material.Then palygorskite/carbon composites were introduced in the car
advanced polymer matrix composites is applied widely in the field of aerospace engineering, autoclave molding process has become one of the primary molding process for composite structure, but this pr
In the processing of fiber placement, due to the coefficient of thermal expansion of the fiber and matrix is not matching and the action of thermos-mechanical loading, caused the shrinkage of fiber/ma
The forming process of composite vane of hollow pipe with large length to diameter ratio was investigated, the method of forming process including co-curing and secondary bonding process.The tools tha
采用板坯铺装模压成型法分别制备了四个目数段即10～20目、20～40目、40～80目和80～120目的杨木纤维增强高密度聚乙烯(HDPE)的木塑复合材料(WPC),并对材料进行了弯曲性能测试、无缺口冲击测试、动态热机械分析(DMA)和24h蠕变-24h回复实验.实验结果表明,增强纤维的尺寸过大或者过小均不利于提高WPC的弯曲性能,增强效果最好的是20～40目纤维增强HDPE复合材料,其弯曲强度达到
通过玻璃纤维线为底线辅助聚乙烯纤维线为面线植入杨木单板强化单板层积材力学性能，对比了植入1cm线性间隔玻璃纤维线的表面处理、网状植入和多层植入杨木单板对单板层积材(LVL)力学性能的影响.结果 表明：通过玻璃纤维硅烷偶联剂表面处理、网状植入和多层植入进一步提高了LVL的弹性模量、静曲强度和冲击韧性，与未植入增强材料的LVL力学性能相比，弹性模量提高了37.4％，静曲强度提高了40.5％，冲击韧性提
为探索木质纤维资源高效利用的新途径,本文提出了基于动态塑化-木塑复合之木质纤维塑性加工理念,系统地研究了木质纤维的动态塑化机理,初步建立了以木质纤维的动态塑化为基础、以木塑复合为基本途径的木质纤维塑性加工的理论体系。主要研究内容包括以下几个方面：(1)通过DMA采用粉末样品夹(MP-DMA)对木材纤维的动态粘弹性进行测试,揭示了离子液体(IL)氯化1-乙基-3-甲基咪唑([Emim] Cl)对木材
苯并噁嗪树脂具有优异的静态和动态力学性能、低的吸水率、高的热稳定性能和阻燃性能等，主要应用于汽车、航空航天和建筑工业材料[1]。天然苎麻纤维具有密度低、力学性能好以及可自然降解等特点，是绿色复合材料的理想增强材料。结合二者各自优势及协同作用，可望制备出高性能苯并噁嗪树脂复合材料。
采用20～40目杨木纤维填充高密度聚乙烯(HDPE)基体,利用板坯铺装模压成型法制备了木塑复合材料(WPC),通过弯曲性能测试和24h蠕变-24h回复实验以及利用两参数指数模型、Findley指数模型以及四元件Burgers模型拟合24h蠕变曲线,研究结果表明,制备的WPC的弯曲强度为26.71MPa,弹性模量为2.73GPa；24h形变为1.142mm,24h回复率为71.45％；三种模型中,四
我国孟宗竹数量约占全球90％，但加工水平却令超过60 wt％的材质沦为竹粉等剩余物。为此将孟宗竹粉(MBF)经γ-氨丙基三乙氧基硅烷(KH550)表面改性并与高密度聚乙烯(HDPE)复合后，提出了竹粉多达50-70 wt％的新型复合材料；采用衍射法(XRD)与电镜法(SEM)诠释了界面演变，借助人工智能(A工)调控了综合性能。