5. CONTRIBUTIONS OF VANADIUM TO PROPERTIES OF HEAT TREATED MEDIUM CARBON FORGING STEELS

CONTRIBUTIONS OF VANADIUM TO PROPERTIES OF HEAT TREATED MEDIUM CARBON FORGING STEELS

来源 :第七届低合金高强度钢国际会议 | 被引量 : 0次 | 上传用户：gaohenghao

【摘 要】

：

Potential benefits of vanadium in heat treated medium carbon bar steels are considered by reviewing examples from several recent studies.Emphasis is placed on microstructural development,strength,and

【作 者】

：

L.M.Rothleutner C.J.Van Tyne R.J.Glodowski J.G.Speer D.K.Matlock 

【机 构】

：

Advanced Steel Processing and Products Research Center The George S. Ansell Department of Metallurgi

【出 处】

：

第七届低合金高强度钢国际会议

【发表日期】

：

2015年11期

【关键词】

：

Induction hardening vanadium microalloying medium-carbon-steels 

下载到本地 , 更方便阅读

下载此文 赞助VIP

声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架

论文部分内容阅读

　　Potential benefits of vanadium in heat treated medium carbon bar steels are considered by reviewing examples from several recent studies.Emphasis is placed on microstructural development,strength,and fatigue performance after conventional and induction heat treating.Potential areas for future research are identified.

其他文献

EFFECT OF HEATING TEMPERATURE ON THE GROWTH BEHAVIOR OF AUSTENITE GRAIN OF TITANIUM MICRO-ALLOYED ST

The behavior of austenite grain growth and the solution of Ti were researched by heated in an electric furnace at the temperature of 850℃ to 1250℃ for 30 min.The precipitates of Ti during the heating

会议

heating temperatureaustenite grain growthprecipitationTi micro-alloyed steel

THROUGH-THICKNESS HOMOGENIZATION IN THIN SLAB DIRECT ROLLING OF Nb MICROALLOYED STEELS

Thick gauge strip production using thin slab casting and direct rolling(TSDR)technologies show important challenges due to the lack of high total reduction from slab to final strip.In these cases,a co

会议

ReductionCritical ThicknessNiobiumGrain SizeAusteniteHomogeneity

MODELLING MICROSTRUCTURE EVOLUTION DURING HOT ROLLING OF HSLA STEELS IN A STECKEL MILL

Microstructure evolution during hot rolling depends on several processing variables.These are the furnace soaking temperature and,for each pass in the schedule,the temperatures,the strains,the strain

会议

ModellingHot rollingNb microalloyed steelsSteckel millMechanical properties

THE INFLUENCE OF VANADIUM MICROALLOYING ON THE PRODUCTION OF THIN SLAB CASTING AND DIRECT ROLLED STE

Vanadium microalloying is highly effective in high strength strip steels produced by thin slab casting and direct rolled process.Because of the high solubility of V(C,N)in austenite,vanadium is likely

会议

VanadiumNitrogenMicroalloyed steelThin slab casting and direct rolling

HOT STRENGTH DURING COILING OF LOW C AND Nb- MICROALLOYED STEELS

The flow stress under typical hot coiling conditions has been quantified for low C and Nb-Ti(V)microalloyed steels.The equation is intended for calculating the amount of bending torque required during

会议

coilingbending torquemicroalloyed steelsMnNbTi(CN) precipitation

EFFECT OF COOLING RATE ON MICROSTRUCTURE AND CENTERLINE SEGREGATION OF A HIGH-STRENGTH STEEL FOR SHI

Ultra-fast cooling(UFC)has been increasingly applied in industry,but accompanying with great changes of rolling strategy.It is therefore of importance to evaluate the characteristics of steels produce

会议

Ultra-fast coolingGrain refinementMicrostructure through thicknessCenterline

INFLUENCE OF FINISH ROLLING TEMPERATURE ON MICROSTRUCTURE AND PROPERTY OF NON-QUENCHED AND TEMPERED

The differences of microstructure and property of non-quenched and tempered bainitic steel under different finish rolling temperatures was analyzed by the methods of color metallographic,scanning elec

会议

Non-quenched and tempered steelFinish Rolling TemperatureMicrostructure and Pr

OPTIMIZATION OF HEAT TREATMENT PROCESS OF HIGH STRENGTH WDL 690D STEEL

Before being subjected to water quenched,16mm WDL690D steel was heated at 910℃,930℃,950℃and 970℃for 20min,40min and 60min,respectively.Microstructures of these samples after heat treatment were observ

会议

WDL690D steelheat-treatmentoptimizationmicrostructuresproperties

STRENGTHENING MECHANISMS OF V-Ti-Mo MICROALLOYED 900MPa HOT-ROLLED FERRITIC STEEL

A new V-Ti-Mo complex micro-alloyed hot-rolled high strength sheet steel was developed by controlling a thermomechanical controlled processing(TMCP)schedule,in particular with variants in coiling temp

会议

Hot-rolled ferritic steelStrengthening mechanismNano-sized carbidePrecipitati

EFFECTS OF HEAT TREATMENT PROCESS ON MICROSTRUCTURE AND MECHANICAL PROPERTIES FOR EXTRA-THICK HIGH-S

To develop thickness>60mm,yield strength>550MPa high-strength steel plate,the effects of heat treatment process on the microstructure and mechanical properties of plate specimens were investigated on

会议

Quenching and temperingHigh-strength steelMechanical propertyMicrostructure