【摘 要】
：
Water Quench technology has been used on certain continuous annealing lines for more than 30 years now to produce HSS grades and the market tendency for higher strength steel grades is accelerating to
【机 构】
：
Research & Development Engineer,Fives Stein,France
【出 处】
：
第十届中国钢铁年会暨第六届宝钢学术年会
论文部分内容阅读
Water Quench technology has been used on certain continuous annealing lines for more than 30 years now to produce HSS grades and the market tendency for higher strength steel grades is accelerating today.Various AHSS grades have been developed for which yield strength and other properties are also considered,to ensure formability.The production of AHSS grades in a continuous annealing line requires a strict cooling control to limit strength deviation within the coil to improve homogeneity and formability.To reach the required AHSS characteristics,Wet Flash Cooling? has been developed,offering a more flexible control of the strip cooling cycle,including initial and final strip temperatures and modulation of cooling rate.This technology has been successfully operating in a large capacity industrial continuous annealing line at a major steel plant for 6 years following its start up in 2009.This paper describes the new challenges of quenching technologies to respond to the evolving AHSS production needs.
其他文献
对重钢一炼钢厂1号板坯连铸机各类漏钢事故的分析,发现黏结漏钢是主要因素.进一步分析发现结晶器液面波动大、SEN潜入深度不合适、生产条件保障不到位及保护渣性能波动等容易造成黏结漏钢的发生,在对1号连铸机发生的漏钢事故进行分析基础上，一炼钢厂进行了防漏钢攻关，提高设备精细化管理水平、制定操作及工艺规范化措施，依靠漏钢预报自动报警以及人工监护，大大减小了漏钢几率。
研究了CSP流程生产的无取向电工钢50W800组织、织构及夹杂物特点,结果表明:(1)成品板为再结晶组织,晶粒尺寸为43.68μm;(2)成品织构以{111}面织构为主,{111}含量达到35.8％;(3)成品板夹杂物以氧化物和硫化物的复合夹杂为主.
利用金相显微镜、TEM等方法分析了不同保温温度和冷却速度对C-Si-Mn-Nb系高强冷轧板显微组织、力学性能和第二相粒子析出行为的影响.结果表明:50℃/s冷速下,保温温度低于800℃时出现带状马氏体,强度高,延伸率较低,超过840℃时铁素体体积分数显著下降,并出现M-A和残奥组织,在820℃时,马氏体组织弥散分布在铁素体基体上,观察到尺寸在7～9nm之间的Nb(C,N)析出物,其综合力学性能最佳
本文对俄罗斯高硅管线钢K52的成分、性能及组织进行了研究,并将其与API X56管线钢进行了对比研究.研究结果表明,K52在成分上采用高硅低锰的成分体系,在强度上与API X56管线钢相近.但K52对塑形和韧性要求更高,要求屈强比≤0.86,-20℃V型冲击功和-60℃的U型冲击功.对于俄罗斯高硅管线钢K52,由于其高硅低锰的成分体系,热轧过程中其氧化铁皮较为严重,较低的出炉温度可以减少氧化铁皮厚
Martensitic advanced high strength steel(MS-AHSS)belongs to a new class of steels that are currently used in the manufacture of lightweight yet crashworthy cars.One issue with using high-strength stee
The hydrogen permeation behaviour of DP and Q&P grades of advanced high strength steels was investigated using the permeability experiments(1)under cathodic charging at different potentials in 0.1 M N
通过对316L不锈钢丝试样的微观组织和表面缺陷进行观察、对表面应力状态进行分析、对试样力学性能进行测试,探究冲压后产品的表面缺陷成因.结果表明:不合格试样的表面缺陷主要有牙齿印、凹坑和擦伤;进口原料试样的抗拉强度为671.4MPa,屈服强度为272.9MPa,延伸率为56.9％,而国产原料试样的抗拉强度为672.9MPa,屈服强度达到287.7MPa,延伸率仅为47.9％;国产钢丝冲压后组织更粗大
The grain refinement of static castings and DC-casting ingots was achieved with a low-voltage pulsed magnetic field setup.Through the study of the interaction between melt and the low-voltage pulsed m
A vertical edger is a critical component of the roughing mill,used to reduce the width of steel slabs.When a vertical edgerexperiences a failure,it directly affects the production of the roughing mill
重钢通过210tLD-RH-CC试生产了7炉W600无取向硅钢,分析了该浇次W600过程[C]变化、两种脱氧方式的合金收得率以及RH最佳工艺时间,为下一步的批量生产提供了技术支持.钢水通过15-20min的深脱碳后，钢中[O]稳定在330ppm～380ppm，[C]基本达到目标要求。其后两种不同的脱氧方式，Al丸的收得率基本相当，而硅铁脱氧的硅收得率大于Al丸脱氧后的硅收得率。RH真空处理时间可以