【摘 要】
:
Producing hydrogen by using semiconductor material with sunlight may become an alternative to future energy source,[1-4] which is considered low/non-carbon and renewable.Co-doping tin dioxide with cer
【机 构】
:
School of Chemistry and Chemical Engineering,South China University of Technology and Key Laboratory
【出 处】
:
第十四届全国太阳能光化学与光催化学术会议
论文部分内容阅读
Producing hydrogen by using semiconductor material with sunlight may become an alternative to future energy source,[1-4] which is considered low/non-carbon and renewable.Co-doping tin dioxide with cerium and antimony can adjust its bandgap, enabling its ability of photocatalysis of hydrogen production. The film of cerium and antimony Co-doped tin dioxide (Ce-ATO) are prepared by sol-gel dip-coating process using a precursor solution synthesized from SnCl2·2H2O as host, and SbCl3 together with Ce(NO3)3·6H2O as dopant precursors.Several times of dipping, drying and pretreating of the film were done before sintering for obtaining higher thickness.
其他文献
Bottom-up strategies for the fabrication of nanomaterials have the advantage of scalability,cost-effective and sustainability,and thus hold great potential to solve the current critical energy and env
受体的结晶状态对 p-i-n 型有机小分子电池的性能具有很大影响。随着制备过程中退火温度的不同,受体分子富勒烯衍生物 SIMEF-Ph,ο-An 可以形成具有不同结晶状态的受体,65℃ 时受体分子与溶剂分子形成共结晶态,120℃ 时受体分子为无序态,180℃ 时受体分子间形成结晶态。我们通过开路光电压实验和变温时间分辨电荷抽取实验研究了受体结晶状态对载流子复合、传输过程的影响,以及当载流子浓度相同
钙钛矿太阳能电池由于高效率、低成本、制备工艺简单等优点而受到科学界的广泛关注.[1]在钙钛矿太阳能电池中,无空穴传输材料钙钛矿电池不仅简化了电池结构,也有利于降低成本,吸引了相当的研究关注.[2-4]在无空穴钙钛矿电池中存在一个金属-半导体界面CH3NH3PbI3/Au,这一界面的性质对于电池性质有很大的影响.[5-6]我们通过旋涂方法在钙钛矿/金电极之间制备一层宽禁带的有机半导体层(N,N,N,
染料敏化太阳能电池[1](DSSC)作为一种新型的太阳能光伏器件,具有传统硅电池所不具备的生产成本低、工艺简单、透明、柔性、色彩可调等优势,在可再生能源利用领域中具有非常广阔的前景.染料是DSSC中的核心部件,设计合成简单高效的染料成为提高DSSC性能的重要途径.我们引入富电子的1,3-二硫杂环戊烯(DTF)作为电子供体(Donor),以10-丁基吩噻嗪(PTZ)[2]作为π-bridge,以2-
作为一种新型的有机-无机杂化纳米材料,陶瓷型脂质体(cerasome)兼具了脂质体(liposome)和二氧化硅纳米粒子的优点。其内部的脂质双分子膜和表面硅氧网状结构决定了陶瓷型脂质体不仅具有较好的生物相容性,同时还可较好的保持稳定的纳米形态,从而使陶瓷型脂质体在生物领域具有广泛的应用前景。本文首次利用陶瓷型脂质体与碲化镉量子点间的静电自组装作用设计、合成了新型荧光陶瓷型脂质体复合材料(QDs-C
Dye-sensitized solar cells (DSCs) are promising candidates for low-cost and clean energy conversion devices.However,Pt counter electrode is a burden for large-scale application of DSCs due to its high
光催化中存在一个典型矛盾:宽带隙半导体通常有较高的光催化性能,然而对可见光响应不佳,从而导致在全太阳光谱的利用效率低[1]。能带结构调控可以有效解决这个问题,通过调整宽带隙半导体的电子能带结构,将光响应区域从紫外光拓展到可见光[2]。
BiOBr系光催化材料因其适合的带隙(2.9 eV),化学稳定性好和相对优越的光催化性能而得到广泛的关注[1,2].研究表明,两种不同半导体单晶材料组成的异质结的内建电场能够抑制光致电子和空穴的复合,提高量子效率 [3].如果将BiOBr和能匹配的半导体制备成异质结光催化新材料,则有希望进一步提高其可见光的光催化活.
低浓度含铀U(Ⅵ)废水[铀酰]因其持久稳定存在、危害范围广、处理难度大,应用传统的废水处理方法无法使低浓度铀U(Ⅵ)彻底消除.例如,吸附和蒸发浓缩法,不但不能有效分离铀U(Ⅵ)反而会产生大量含铀U(Ⅵ)的污泥,易造成二次污染,且运行成本较高;化学沉淀法和还原法过程中易产生沉淀物,二次处置难度较大;生物处理法因铀U(Ⅵ)对微生物的毒性高及选择性强而不能达到理想的去除效果.光催化还原技术具有绿色、反应
Titania (titanium dioxide, TiO2) has attracted tremendous attentions as a semiconductor photocatalyst in the past decades due to its superior features including chemical stability, low cost, high reus