LiMn1-xFexPO4 nanomaterials at low Fe concentration(x = 0,0.1,0.2)for lithium-ion batteries have been synthesized via a facile solvothermal route in a mixed solvent of water and polyethylene glycol(PEG200).SEM and TEM images reveal that all samples are single crystalline with similar rod-like shapes,and XRD characterizations indicate that the crystal lattices decrease with the increasing concentration of Fe.