  Organic-inorganic halide perovskite possess excellent chemical,optical,and electronic properties that make them attractive for next-generation solar cells.Formamidinium-based (FA-based) perovskite has been demonstrated to have improved thermal stability and broadened absorption region compared to methylammonium-based (MA-based) analogues.An important target for the further improvement of perovskite-based solar cell is to eliminate or reduce the use of heavy metal lead.
其他文献
以液态硅氧烷和氧化铝为原料,采用乳状液模板法制备了多孔刚玉-莫来石陶瓷,研究了氧化铝加入量(分别为45、60、75、90g)和烧结温度(1450、1500、1550、1600、1650℃)对多孔陶瓷性能的影响.结果表明:硅氧烷热解氧化生成方石英与氧化铝莫来石化反应在1500℃基本完成.随着氧化铝粉加入量增加,多孔刚玉-莫来石陶瓷密度为1.55~2.12g·cm-3.多孔陶瓷平均孔径分布从0.5到2
采用不烧技术制备了镁尖晶石不烧砖,利用扫描电镜对其显微结构进行了分析.结果表明:高温下砖中原位生成尖晶石,从而在基质中形成了一定粒度梯度的尖晶石,使得砖基质致密,具有较高的高温抗折强度.该砖在武钢进行了工业试用,结果表明:RH精炼炉无铬耐材的使用寿命与同期镁铬砖相当,为武钢进行RH无铬化生产打下坚实基础.
分析了LT法除尘灰的性能,并研究了冷压成球所需的结合剂和成球工艺,冷压球在上海梅山钢铁股份有限公司钢厂得到回收利用,平均每月回收利用量在6000t左右,既为梅钢创造了经济效益,又实现了资源的回收利用.
以不同粒度的用后滑板回收料为原料,分别用酚醛树脂、液体水玻璃和磷酸二氢铝作结合剂制作铁水包工作衬材料,研究了结合剂对该材料性能的影响.研究结果表明:酚醛树脂是用后滑板回收料制作铁水包工作衬最好的结合剂,但从经济成本和性能考虑,采用磷酸二氢铝为结合剂的滑板回收料制品完全可以取代黏土砖来做铁水包工作衬用耐火材料.
Organic-inorganic hybrid lead halide perovskite are very promising materials for high-efficiency solar cells.However,these materials suffer from moisture instability which would decompose into PbI2,an
TiO2 is one of the best choices for electron transport layer in perovskite solar cells (PSCs),due to its the perfect match of band structure between TiO2 and perovskite,simple preparation process,good
Organometal halide perovskite solar cells (PSCs) have triggered enormous research tide in recent years due to their high carrier mobility,long charge diffusion length,intense broadband absorption,faci
Methylammonium lead iodide CH3NH3PbI3 (MAPbI3) perovskite solar cells (PSCs) have become the forefront of photovoltaic technologies.The MAPbI3 are in the form of thin films in most PSCs equipements,bu
会议
电子传输层对平面结构钙钛矿电池的有效运行至关重要.本文用PW12-TiO2 复合物在FTO 玻璃/ PW12-TiO2/钙钛矿/spiro-OMETAD/Au 器件结构中作为电子传输层.导带最小值(CBM)的适当下降增强了电子从钙钛矿向PW12-TiO2 复合层的提取.结果TiO2 基平面结构钙钛矿电池中通常存在的瓷砖效应被显著抑制了,并且开路电压增加到了大约1.1V.用PW12-TiO2 作为紧
低成本与简单的制备工艺使得钙钛矿太阳能电池特别有吸引力.我们用低温溶液法制备了一种无空穴传输层高效的ITO/CH3NH3PbI3/PCBM/Al 结构的钙钛矿太阳能电池.这种无空穴传输层的电池的光电转化效率超过了11%,这基本上接近有PEDOT:PSS 的钙钛矿太阳能电池光电转化效率.这种无空穴传输层的钙钛矿太阳能电池有一个特点开路电压可以达到1.06V,43 个器件的平均电压值达到了1V.我们用