The interaction between mechanics and electrochemistry in extremely thin electrodes

来源 :国际腐蚀工程大会(ICEC2016) | 被引量 : 0次 | 上传用户：ullige000

【摘要】

：

　　During corrosion,mechanics and electrochemistry interact always to each other.Although there are thermodynamic studies about the stress-caused change in equ

【作者】

：

Tong-Yi Zhang Sheng Sun

【机构】

：

MaterialsGenomeInstitute,ShanghaiUniversity,Shanghai200444,China

【出处】

：

国际腐蚀工程大会(ICEC2016)

【发表日期】

：

2016年8期

下载到本地 , 更方便阅读

下载此文赞助VIP

声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架

论文部分内容阅读

　　During corrosion,mechanics and electrochemistry interact always to each other.Although there are thermodynamic studies about the stress-caused change in equilibrium potentials,few multiscale computations have been reported in the literature.

其他文献

含碳球团加热过程析出特性的实验研究

　　针对含碳球团的加热过程，通过实验方法，探究了升温速率、含铁原料、碳氧比及还原剂(焦炭与无烟煤)等对含碳球团失重与析出特性的影响。研究表明：升温速率、含铁原料性质、还

会议

转底炉含碳球团析出特性实验研究

喷雾热解过程中NiO粉体与尾气反应的热力学研究

　　本文以NiCl2 水溶液为原料，采用喷雾热解法制备NiO 粉体材料.XRD 检测发现所制备NiO 粉体中存在氯化镍含水化合物NiCl2·xH2O.从热力学角度分析了NiO 粉体中残氯的存在机

会议

氯化镍氧化镍喷雾热解热力学残氯

预还原镍红土矿在Cl2-O2中选择性氯化热力学分析

　　本文对预还原褐铁矿型镍红土矿在Cl2-O2 气氛中选择性氯化进行了热力学分析。通过计算绘制不同温度下Fe(Ni,Co)-Cl2-O2 体系热力学平衡相图,发现存在热力学区域使Fe2O3、

会议

镍红土矿Cl2-O2气氛流态化选择性氯化铁的抑制

The Role and Character of Micro-Fracture Events in Determining Crack Growth Rate

　　This paper explores the role and character of the micro-fracture events occurring at the crack tip in determining crack growth rate in steels under tensile

会议

Localized Corrosion of Mild Steel in a CO2 Aqueous Environments-Causes and Mechanisms

　　Localized CO2 corrosion is a non-uniform loss of metal from the internal pipe wall which can lead to a loss of containment in oil and gas facilities.

会议

Effect of Hydrogen on Pitting and Stress Corrosion Cracking

　　Hydrogen could enter into metals in many processes such as steel making,welding,pickling,the heat treatment in hydrogen gas,cathodic protection,storage in m

会议

Corrosion Survey and Control Strategies in China

　　In the 21st century,both the economic aggregate and the industrial structure have changed greatly.A program to evaluate the corrosion situation and strategy

会议

Recent understanding of the hydrogen influence of medium strength steels

　　Research on the influence of hydrogen is an ongoing topic for the last 20 years.We developed the Linearly Increasing Stress Test(LIST)that has significant a

会议

Environmental Degradation of Metals and AlloysSurface Analytical Approach,Mechanisms,and Modeling

　　The understanding of the interactions of metal and alloy surfaces with their environment is a key for the control of environmental degradation of materials

会议

How to control inter-diffusion between coatings and substrates at high temperatures

　　The inter-diffusion between coatings and substrates at high temperatures significantly influences the mechanical properties of alloys,especially for TiAl in

会议

The interaction between mechanics and electrochemistry in extremely thin electrodes

与本文相关的学术论文