【摘 要】
:
Graphitic carbon nitride(g-C3N4) polymer has been demonstrated as a kind of advanced support material for Pt-based NPs due to its excellent mechanical resistance and anticorrosion ability in acidic an
【机 构】
:
School of Chemical Engineering and Technology,Harbin Institute of Technology,No.92 West-Da Zhi Stree
论文部分内容阅读
Graphitic carbon nitride(g-C3N4) polymer has been demonstrated as a kind of advanced support material for Pt-based NPs due to its excellent mechanical resistance and anticorrosion ability in acidic and oxidative environments,[1] as well as the abundant Lewis acid and base sites(terminal and bridging NH-groups and lone pairs of N in triazine/heptazine rings,respectively) that are potential anchoring sites for Pt[2]and adsorption sites for CO.
其他文献
针对传统镍基阳极存在的问题,具有良好的耐硫毒化、抗碳沉积、氧化还原稳定性和尺寸稳定性的La0.2Sr0.8TiO3+δ(LST)阳极材料成为研究的热点之一,已取得了一些有意义的成果.考虑到LST具有较好的力学强度,在还原气氛下具有较高的电子传导性和较低的离子传导性,不适合单独用作SOFC阳极.
Introduction High temperature steam electrolysis(HTSE) through solid oxide electrolysis cell(SOEC) is thought to be one of the most promising processes to produce massive hydrogen with low or zero CO2
Hydrogen has been considered as a clean energy resource to replace the diminishing fossile fuel.Electrochemical water splitting is a well-established commercial technology to convert electricity produ
纳米电催化剂的催化性能主要决定于其本身的电子结构及表面结构,因此通过调节纳米电催化的表面结构和组成,包括尺寸、形貌及暴露晶面可以有效提高其电催化活性[1].近年来,人们已通过各种化学、物理方法设计、制备了各种组成和形状的金属纳米晶体电催化剂,用于燃料电池的阳极和阴极电催化.除了电催化剂本身性能外,载体对其催化性能同样会产生重要影响[2].
Nickel hydroxide is a representative cathode material for alkaline secondary batteries that includes two types:α-and β-Ni(OH)2.Generally,α-Ni(OH)2 shows more reversible capacity because the average ox
Three-dimensional graphene based materials(3DGs) are emerging as a new class of ultra-light and porous carbon materials because of its unique structure and fascinating properties such as interconnecte
To fabricate and control the micro-and nano-structures in 3D scales is able to render unique properties for traditional functional materials.There are many nanofabrication techniques including chemica
由于具有较快的电极反应动力学,可以采用非Pt等稀贵金属,降低成本,同时具有缓解碳酸盐化等优点,碱性阴离子交换膜燃料电池( alkaline anion exchange membranes,AAEMFCs)得到了较深入的研究.作为AAEMFCs中关键部件,碱性阴离子交换膜(alkaline anion exchange membranes,AAEMs)成为限制AAEMFCs广泛应用的一个重要因素.
通过枝接改性的方法制备聚砜-膦酸(PSF-PA)/聚砜-1,2,3-三氮唑(PSF-Tri)酸碱复合膜,聚砜-膦酸的制备经过三溴化-膦酸化-水解反应完成;聚砜-1,2,3-三氮唑的制备经过氯甲基化-叠氮化-1,3-环加成反应完成.依照不同比例将酸性聚合物和碱性聚合物均匀混合后,高温高压下压制成膜.
质子交换膜在燃料电池中起到传输质子和隔离阴阳极反应物的作用,但是目前的商业化质子交换膜,如Nafion膜,存在严重的燃料渗透(特别是对液体燃料,如甲醇等)的问题,因此严重限制了以甲醇为燃料的直接甲醇燃料电池(DMFC)的发展.DMFC中甲醇的渗透不仅使得燃料利用率的大大降低,同时甲醇渗透至阴极带来的混合电位更会显著降低DMFC的能量输出效率.因此,高性能阻醇质子交换膜成为质子交换膜研究的热点,但常