【摘 要】
：
This work focuses on the production of a new composite material using Yellow River sediment and coal slime ash via alkali-activated method.XRD,FTIR and SEM/EDS were used to characterize the alkali-act
【机 构】
：
School of Civil Engineering, Dalian University of Technology, Dalian 116024, China
【出 处】
：
中国大坝工程学会水库泥沙处理与资源利用技术专业委员会成立大会
论文部分内容阅读
This work focuses on the production of a new composite material using Yellow River sediment and coal slime ash via alkali-activated method.XRD,FTIR and SEM/EDS were used to characterize the alkali-activated products and microstructure of the composite material.Compressive strength was tested to characterize the mechanical property of the composite material.It was found that,the compressive strength of the Yellow River sediment-coal slime ash composites increases as the added Ca(OH)2 content grows.The compressive strength increases fast in the early stage but slowly after 28 days.The strength of the composites can be significantly improved via the addition of small amount of NaOH and gypsum.The products (C-S-H,ettringite and CaCO3),especially C-S-H,make much contribution to the enhancement of strength.The highest strength of the composites could reach 14.4 MPa after 90 days curing with 5% Ca(OH)2,0.2% NaOH and 7.5% gypsum.The improved properties of the composites show great potential of utilizing Yellow River sediment for inexpensive construction materials.
其他文献
挑流消能是高坝广泛使用的一种消能方式,但是由于高速水流运动的复杂性和下游基岩冲刷的重要性,挑流鼻坎的体型的选择尤为重要.本文以某水利工程为依托,利用模型比尺为1∶50的物理模型,进行动床试验,研究不同上游水位下,五种不同的挑流鼻坎体型对下游冲坑深度和冲坑分布的影响.试验结果表明,挑坎体型方案五能形成较好的冲刷坑,即当中孔右边墙半径300m、加设长短轴半径分别为6.55m和4.8m的舌型挑坎,2＃表
Preparation of homogeneously dispersed graphene has significant impact on its application.In this research,graphene nanoplatelets (GNPs) were uniformly dispersed in aqueous solution by means of sonica
水库清淤可以减缓水库淤积速度,延长水库的寿命.在库区内设置带有吸泥头并能移动的管道,利用水库自然水头,将库区淤积泥沙通过管道输送至库外的方式,具有排沙效率高,耗能小的优点.分析了一些中小型水库的运用实例,探讨其移植到大型水库的可能性及需要研究解决的关键问题.
Preparing highly homogeneous and stable aqueous graphene nanoplatelets (GNPs) suspension is significant for practical applications.In this study,non-covalent modified GNPs in aqueous solution were pre
分析了管道高浓度泥沙输移基本规律,基于弗劳德相似准则及雷诺相似准则,提出了管道流型处于阻力光滑区条件下含沙量换算关系.分析认为,由于原型和模型含沙量存在差别,浑水密度不一致,致使水头损失出现偏差,需要进行阻力校正,校正方法可根据密度差异调整动力黏滞系数比尺达到阻力相似的目的.
The homogenous graphene nanoplatelets (GNPs) suspension had been prepared through ultrasonic exfoliation in the presence of methylcellulose (MC) as dispersant.In the work,the influence of different so
分析了小浪底库区管道排沙大范围清淤、高强度输沙清淤及坝前小范围清淤等三种主要方式,认为:坝前小范围清淤方式技术难度低、可行性高,可以长期保持坝前5km内不产生泥沙淤积;合理地进行系统操作,提高管道排沙系统效率,将会进一步降低清淤单价.
为了解决蓄水与水库淤积的矛盾,设计了在库区淤泥清除管道系统上使用的水库自吸式排沙管道吸泥头吸泥浓度控制装置.结果表明,通过控制管道入口与浆体液面的位置关系,在管道排沙运行时可准确、稳定地控制管道泥沙浓度,从而使排沙管道系统安全、高效地运行.
对小浪底水库自吸式管道排沙系统的管道材料选取、管道连接方式、铺设施工工艺和管道过坝施工技术等进行了研究,认为U-PVC缠绕管材可满足排沙管道要求,在日前的设备技术条件下,管道施工有成熟的实施条件.同时,对管道铺设方式和与过坝隧洞连接等施工关键问题提出了相应的解决方法.
In this work,the effects of the non covalent surface modification method on the dispersion of graphene nano-sheets (GNS) in water and chloride diffusion of the cement paste incorporating these dispers