【摘 要】
：
本文通过合成了一种新型的聚羧酸系高性能减水剂,并与市售聚羧酸系高性能减水剂进行了对比,研究表明,该减水剂优于市售聚羧酸系高性能减水剂。同时,本文采用该剂种配制了C20～C
论文部分内容阅读
本文通过合成了一种新型的聚羧酸系高性能减水剂,并与市售聚羧酸系高性能减水剂进行了对比,研究表明,该减水剂优于市售聚羧酸系高性能减水剂。同时,本文采用该剂种配制了C20～C50混凝土,并与萘系减水剂进行了对比,该剂种达到或超过了萘系减水剂的性能,且其与萘系减水剂相比具有较高的经济优势。
In this paper, a new type of polycarboxylate superplasticizer was synthesized and compared with the commercially available polycarboxylate superplasticizer. The results show that the superplasticizer is superior to the commercial polycarboxylate High performance water reducer. In the meantime, C20 ~ C50 concrete was prepared with this kind of agent, and compared with naphthalene superplasticizer, the agent met or exceeded the performance of naphthalene superplasticizer, and compared with naphthalene superplasticizer Has a high economic advantage.
其他文献
研究了粉煤灰混凝土(FAC)、高性能混凝土(HPC)和高性能混杂纤维增强膨胀混凝土(HPHFREC)在5％MgSO4溶液的化学腐蚀和弯曲应力腐蚀作用下的物理力学性能变化。实验结果表明，混凝
采用快冻法研究了研究高强混凝土(HSC)和大掺量矿物掺合料混凝土(HVMAC)在水和5％MgSO4(质量分数)溶液中的抗冻性。结果表明：对于较高水胶比、低掺量矿物掺合料的HSC，MgSO4溶液因
根据濒海地区环境荷载特点，本文提出了针对既有混凝土结构的耐久性状态分析方法，从全寿命分析角度建立了预测其剩余寿命的模型，并得到工程实践验证。
本文简要介绍了C35混凝土在大体积基础筏板的工程实践。由于大体积混凝土水化温升过高，易导致混凝土温度应力引起的裂缝产生。经过优化配合比，降低水泥用量，进行混凝土内部温度
通过收集全国范围内的混凝土施工配合比，在对数据进行统计、分析的基础上，指比其不足，又对主要区域的混凝土配合比进行实地调研及试验验证，得出混凝土配合比中主要参数的用量范围
１９９９年，对个旧市市属医院、社会办医院、厂矿卫生所、乡镇卫生院等８９所医疗单位消毒质量进行了调查。检测时，对室内空气用平板沉降法采样，以细菌总数≤２００ ｃｆｕ／ ｍ３（ Ⅱ类场所）或≤５００ ｃｆｕ／ ｍ３（Ⅲ类场所）为合
本文以高模量抗车辙沥青混凝土、多孔排水降噪沥青混凝土、阻燃沥青混凝土的特点探讨了功能性沥青路面新材料的研究与应用。功能性沥青路面新材料的开发和应用大为提升了我国
1994年以来 ,对威海市一次使用性卫生用品共采样 2 2 7份 ,进行细菌污染检测。以细菌总数≤ 2 0ｃｆｕ/ ｇ、不检出大肠菌群及致病菌为合格。结果 ,卫生巾合格率为 81 2 5 % ( 39/48
近来,全党全国正在深入学习贯彻江泽民总书记关于“三个代表”的重要思想,“三个代表”是新时期全面加强党的建设和实现中华民族复兴的伟大纲领,是推进跨世纪各项工作的行动
采用(甲基)丙烯酸／甲氧基聚乙二醇(甲基)丙烯酸酯的酯类单体混合物与烯丙基聚醚或甲基丁烯基聚乙二醇等不饱和醚类单体，通过分子设计合成得到一种缓释型聚羧酸系减水剂(SRPC)。