Phase Transition of Ball-Milled Ni50-xMn37ln13Cox (x=0,5) Alloy Powders

来源 :2014中国功能材料科技与产业高层论坛 | 被引量 : 0次 | 上传用户：lvjjvl

【摘要】

：

Ni50-xMn37In13Cox (x=0,5) alloy powders were obtained by ball-milling from the corresponding ribbonprecursors.The as-milled NixMn37In13 and Ni45Mn37In13Co5 powders show disordered fct and fcc structur

【作者】

：

Feng Xu Xiaoping Fei Wei Li Jun Liu Guodong Tang Weishi Tan Shandong Li

【机构】

：

School of Materials Science and Engineering,Nanjing University of Science and Technology, Nanjing 21

【出处】

：

2014中国功能材料科技与产业高层论坛

【发表日期】

：

2014年2期

【关键词】

：

Martensitic transformation Phase transition Ball-milling Powder

下载到本地 , 更方便阅读

下载此文赞助VIP

声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架

论文部分内容阅读

其他文献

A Flexible Piezoresistance Strain Sensor based on a single ultralong Tellurium micrometer wire

Flexible strain sensors based on a single ultralong Tellurium micrometer wire have been prepared.The strain sensor device consists of a flexible polystyrene substrate with a single Telluriun micromete

会议

Strain SensorTemicrometer wirePiezoresistance effectSchottky barrier

TiO2光催化剂负载膨润土材料的制备及催化降解研究

采用溶胶凝胶法制备了TPBM材料。利用单因素法研究了反应时间、反应温度以及钛酸丁酯的量等工艺参数对所制备材料降解甲基橙效果的影响，以及降解过程与甲基橙溶液浓度和光照时间之间的关系。

会议

TiO2膨润土插层光催化剂

Electrochemical Properties Test of Vanadium Electrolyte Containing V (Ⅲ) and V (Ⅳ) Ion

The electrochemical behavior of vanadium solution containing V (Ⅲ) and V (Ⅳ) ion each 50% was characterized by cyclic voltammetry and chronopotentiometry with different working electrodes, temperature

会议

vanadium redox batteryelectrolytecyclic voltammetryreversibilityelectrochemi

预烧方式对锰锌铁氧体材料性能影响

采用氧化物法制备锰锌铁氧体，研究了不同预烧方式对材料电磁性能的影响。结果表明，相同预烧温度情况下，回转窑预烧粉体尖晶石相更多，导致材料的功率损耗升高。

会议

锰锌铁氧体预烧功率损耗尖晶石型铁氧体

Synthesis and Characterization of Polyvinylpyrrolidone modified Bentonite and Its Application in Sup

The modified bentonite was prepared via solution intercalation using sodium bentonite and a series of polyvinylpyrrolidone (PVP) as raw material and intercalation agents, respectively.

会议

bentonitesuperabsorbent polymerwater absorbencypolyvinylpyrrolidone

Hollow Polymer Nano-latex Microspheres Prepared by In-situ Polymerization with the Method of Encapsu

In this paper, the hollow polymer nano-latex microspheres with uniform size and good monodisperse made by in-situ polymerization with the method of encapsulation non-solvent, and the effect of crossli

会议

In-situ polymerizationHollow polymerLatex microspheresCrosslink monomerSwell

Magnetization and giant magneto-impedance effect of Co-richmicrowires under different driven current

Co68.25Fe4.5Si12.25B15 amorphous microwires with a diameter of 34 μm wereprepared via the melt extraction method.The dependency of AC driving current Iac on giantmagneto-impedance (GMI) effect and mag

会议

Amorphous microwireGMI effectmagnetizationdriving current

不同气氛下ZrB2-SiC复合陶瓷发热元件临界温度及电性能研究

以ZrB2和SiC超细粉体为主要原料，经热压烧结和线切割加工制成ZrB2-SiC复合陶瓷发热元件，利用XRD及SEM分析了该复合陶瓷的微观结构。通过不同高温实验考察了发热元件分别在氩气、空气和氮气气氛下的表面侵蚀程度与温度的关系并确定其对应的临界温度。

会议

ZrB2-SiC复合陶瓷发热元件气氛临界温度温度电性能

Deposition and antibacterial properties of Ag nanoparticles on dopamine coated carbon nanotubes

In order to reduce the releasing rate of nanosilver in solutions, the carbon nanotube was selected to combine with nanosilver.The higher dispersion of Ag nanoparticles (AgNPs)was in-situ prepared on t

会议

Silver nanoparticlesMWNTDopamineAntibacterialproperty

Analysis of solvent properties of mandarin oil

Mandarin oil were extracted twice to ensure the purity of limonene, respectively.The spectrum testandSolvent solubility of chemical analysis indicate that it is a certain fluorescence effect and the u

会议

recyclingoptical spectroscopypolymeric biomaterialsoptical absorptionorange

Phase Transition of Ball-Milled Ni50-xMn37ln13Cox (x=0,5) Alloy Powders

与本文相关的学术论文