论文部分内容阅读
With the development of the microwave absorption technology,material science engineers are getting more and more interests in microwave absorbing materials(MAMs)due to their extensive applications in terms of electromagnetic(EM)materials.The MAMs can be used to attenuate and absorb the EM waves by converting the EM energy into heat or any other forms of energy to reduce the transmission and wave reflection.In recent days,human’s life becomes the part of the MAMs applications like buildings,cloths,anti-radiation appliance,stealth coating,vehicles and warship.Many applications of MAMs are working to protect human beings in terms of health,prevention of harmful EM interference,and also used to protect radar detection.The increasing application of MAMs,needs to satisfy the updated requirements for human protection.To understand the microwave absorption properties like dielectric loss,magnetic loss,conductive loss,permittivity and permeability of the composite by changing combination-based behavior of the composite.The key factor behind the improving response for the absorption performance of the absorbent is to improve impedance matching and energy attenuation.In the GHz frequency range,the permeability of the material is usually much smaller than the dielectric constant.Therefore,it is required to increase the permeability of the material to improve impedance matching and increase energy attenuation.In this work,carbonyl iron particles(CIP)with basalt sheet(B)are fabricated by using waterborne polyurethane(PU)coatings to perform highly efficient microwave absorption.The characteristics(electromagnetic,microwave absorption)of CIP and B were measured in2–18 GHz by a technology(transmission/reflection).The arch method is used to measure the reflection loss against specific thickness composite coating.A comprehensive discussion provided to understand the electromagnetic(EM)loss mechanism as well as the effect of B on the properties of the composite.The scanning electron microscopy(SEM)and transmission electron microscopy(TEM)utilized to observe the morphology and micrographs of the considered coatings.Magnetic moment of the sample is measured in the presence of uniform magnetic field via perpendicular vibration of material.Minimum range in change(10-5 to10-6)can it measure(detect)via VSM.In this research work,we provide satisfactory improvement towards least usage of CIP due to the unique properties of B and efficient output against electromagnetic attenuation.The limitations of CIP composite towards absorption properties are optimized by applying the basalt sheet with CIP with efficient(small or less)thickness.Coating thickness varies from 0.8mm to 1.2mm to understand that how the best results can be obtained.The magnetic properties as well as reflection loss is affected by the size,thickness and molar ratio of basalt and CIP.Many samples on the basis of thickness,size and content ratio analyzed via experimental results.The increasing molar ratio of basalt(0.1to0.5)in samples and increasing thickness(1.2 mm)reduce the reflection loss due to improve in impedance matching.Improved impedance matching causes a major contribution towards the reduction in reflection loss of focused material.That contribution causes a major improvement the higher response of microwave absorption property.By taking size,thickness and samples content ratio of considered composite,we introduce the suitable ratio of basalt to get absorption peak(-34 d B)at 11.8 GHz frequency and applied thickness is 1.2 mm(3.6GHz efficient bandwidth).The composite(CIP:B:PU),build to understand the EM loss effects to improve the broad band absorption properties.