Electrochemical insertion/extraction of Li on cathode materials of anatase type TiO_2, quasilayered structure V_2O_5 and layered structure MoO_3 was measured on samples of which structures were well characterized and showed a wide range of crystallinity. On the basis of experimental results on structure, morphology and charge-discharge characteristics, the effect of crystallinity of the cathode materials on electrochemical Li insertion/extraction pedermance was discussed. These three transition metal oxides were classified as one group on the basis of whether the crystallinity of these oxides affects to the performance or not; LiMn_2O_4 and LiCo_(0.5)O_2 belongs to the former group and TiO_2, V_2O_5 and MoO_3 to the latter. Electrochemical insertion / extraction of Li on cathode materials of anatase type TiO_2, quasilayered structure V_2O_5 and layered structure MoO_3 was measured on samples of which structures were well characterized and showed a wide range of crystallinity. On the basis of experimental results on structure, morphology and charge-discharge characteristics, the effect of crystallinity of the cathode materials on electrochemical Li insertion / extraction pedermance was discussed. These three transition metal filters were classified as one group on the basis of whether the crystallinity of these soot effects to the performance or not; LiMn 2 O 4 and LiCo 0.5 O 2 belongs to the former group and TiO 2, V 2 O 5 and MoO 3 to the latter.