【摘 要】
:
Phase structure characteristics near the interface of Fe3Al/Q235 diffusion bonding are investigated by means of X raydiffraction (XRD), transmission electronic
【机 构】
:
Key Lab of Liquid Structure and Heredity of Materials,National Key Lab of Advanced Welding Productio
【基金项目】
:
the Visiting Scholar Foundation ofNational Key Laboratory of Advanced Welding Production Tech-nology;Harbin Institute of Technology, People’s Republic of China
论文部分内容阅读
Phase structure characteristics near the interface of Fe3Al/Q235 diffusion bonding are investigated by means of X raydiffraction (XRD), transmission electronic microscope (TEM) and electron diffraction, etc. The test results indicatedthat obviously a diffusion transition zone forms near the interface of Fe3Al/Q235 under the condition of heatingtemperature 1050~1100℃, holding time 60 min and pressure 9.8 MPa, which indicated that the diffusion interfaceof Fe3Al/Q235 was combined well. The diffusion transition zone consisted of Fe3Al and α-Fe(Al) solid solution,Microhardness near the diffusion transition zone was HM 480~540. There was not brittle phase of high hardness inthe interface transition zone. This is favorable to enhance toughness of Fe3Al/Q235 diffusion joint.
其他文献
A model of double grains under plane stress state has been established. According to the double grain model, thermal stress induced by thermal cycling in weldin
In order to reduce high calibration pressure in hydroforming of components with too small radii, a method wasproposed to manufacture automotive hollow component
A mathematical model for the three-dimensional simulation of free dendritic growth and microstructure evolutionwas developed based on the growth mechanism of cr
The influence of external field(magnetic field and stress field) on the transformation strain of Ni52.9-Mn24.4Ga22.7 single crystal were investigated and its me
A high-Fe containing aluminum matrix filler metal for hardfacing aluminum-silicon alloys has been developed by using iron,nickel,and silicon as the major streng
The research on numerical simulation for combinative process of SPF/DB is carried out in this paper. The contacting problem of sheets is analyzed by using the p
The problem of instability in polycrystalline ordered double-perovskite Sr2FeMoO6, is presented in this paper. By the X-raydiffraction analysis and the measurin
Blade precision forging is a high temperature and large plastic deformation process. Interaction of deformation andheat conduction results in producing large te
Hexagonal AIN films have been obtained by arc ion plating at different negative biases. X-ray diffraction and scanningelectron microscopy results show that AIN
Vacuum diffusion bonding of TiB2 cermet to TiAl -based alloys using Ni interlayer has been carried out at 1123~1323 K for0.6~3.6 ks under 80 MPa. The effects of j