【摘 要】
:
An electromagnetic anti-fouling technology(EAFT) was developed further. The operating principle of the EAFT was presented using fundamental physics laws. To val
【机 构】
:
College of Environment and Energy Engineering
【基金项目】
:
the National Key Fundamental Research and Development Program of China
论文部分内容阅读
An electromagnetic anti-fouling technology(EAFT) was developed further. The operating principle of the EAFT was presented using fundamental physics laws. To validate the effect of EAFT and identify the mechanism, a circulating flow setup was built. A series of fouling tests were carried out with and without EAFT, measuring fouling thermal resistance as function of time, making scanning electron microscope images and analyzing the particles size distribution in solution by dynamics light scattering technology. The main results were as follows: 1)All the precipitated crystals in solution were calcite and there were little differences between with EAFT and without EAFT in the experimental range. 2) The number of precipitate nucleation in solution was small and the particle growth was slow without EAFT. In opposition to the case untreated, a rapid particle growth was observed and the number of nucleation was expected to be large, due to the fact that the EAFT effectively increases the ions and crystals collision frequency and effectiveness by utilizing the induced electric field. It is indicated that the particle growth is promoted mainly by coagulation process but not nucleation growth. 3) The EAFT could prolong the delay time of fouling greatly, and after the delay time, the thermal resistance quickly increased. Therefore, in order to mitigate scale significantly, the floccules in solution should be deposited beforehand in a low-lying area of the exchangers and let off in time.
其他文献
Enantioseparation of salbutamol solute was carried out in liquid-supported membrane by using a polyvinylidene fluoride hollow-fiber module. The enantioselective
Surface preparation is potentially important to the corrosion and biomedical properties of NiTi shape memory alloys.The effect of surface preparation on corrosi
A new cathode material fabricated by solid state reaction method was reported. The SmVO4 powder was obtained by firing the mixture of Sm2O3 and V2O5 powders in
Statistical model of magnetization reversal was used to simulate the magnetization reversal behavior in the sintered Nd-Fe-B magnets with double grain-size dist
A nozzle clogging online forecasting model based on hydrodynamics engineering was developed, in which the actual flow rate was calculated from the mold width, t
Fe100-xPtx(x=30at.%-60at.% ) nanocomposite films were deposited on natural-oxidized Si(100) substrates by magnetron sputtering. The as-deposited films were anne
CoPt nanoparticles were prepared by simultaneous thermally reducing Co(CH3COO)2 and Pt(acac)2 in oleylamine with a small quantity of oleic acid. The composition
Er doped ZnO thin films were grown on Si substrates using SiO2 buffer layer by pulsed laser deposition (PLD) method.The obtained films crystallize well and show
The microstructure and characteristics of pre-sintered strontium ferrite powderwere investigated by X-ray diffraction, scanning electron microscopy and transmis
Cu-Zn, Cu-Zn-Sn, Cu-Zn-Ni alloys were melted by vacuum smelter. The effect factors to the surface free energy of the alloys such as chemical composition, crysta