【摘 要】
：
Comparing and analyzing some volume deformation measuring means for cement-based materials at home and abroad, a continuous online monitor of cement-based mater
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
Comparing and analyzing some volume deformation measuring means for cement-based materials at home and abroad, a continuous online monitor of cement-based material volume deformation in multiple environments is developed. The device is designed based on the environmental simulation technology, micro-distance measuring technology of laser and eddy current, and transmission agent online monitoring the deformation of multi-group samples. This device can be used widely, such as glass, ceramics, walling material, and so on, with high precision, low testing cost, and intellectualization.
其他文献
To investigate the treating parameters influence on the surface roughness of the MAO ceramic coating on AZ91D, experiments were implemented in the alkaline elec
Al2O3/TiAl composites were fabricated by PAXD (pressure-assisted exothermic dispersion) method. The effects of Nb2O5 content on the microstructure and mechanica
Through the addition of rare earth oxides into the coating of electrodes, the high temperature oxidation and sulphidation resistance of weld metal were studied.
Effect of cooling rate on both microstructure and room temperature compressive performance of the AZ91 magnesium alloy was investigated. The experimental result
Honeycomb-like superstructures consisting of ZnS nanosheets with uniform thickness of about 20nm and lateral dimension of several micrometers were built up from
For large-sized AISI P20 steel block used as plastic die with a thickness of more than 200 mm, appropriate quenching processes are the key to obtain much thick
Mg65Cu25Gd10 amorphous alloy powders were synthesized by mechanical alloying (MA). The most suitable process is that the milling velocity is 600 r/min and the m
The evolution of configurations of Aln (n=3,4,6,13,19) clusters were investigated using linear synchronous transit (LST) method. The stable structures of Al3,Al
Under electron beam irradiation, the in-situ formation of 2H-SiC dentritic nanocrystals from amorphous silicon carbide at room temperature was observed. The hom
Thin films of Nd3+/V5+-cosubstituted bismuth titanate,(Bi3.5Nd0.5)( Ti2.96V0.04)O12 (BNTV),were fabricated on the Pt(111)/Ti/SiO2/Si(100) substrates by a chemic